Dy3+掺杂SrGdGa3O7晶体的晶体生长, 结构、光学和可见光荧光特性
|
王海东, 王燕, 朱昭捷, 李坚富, LAKSHMINARAYANA Gandham, 涂朝阳
|
Crystal Growth and Structural, Optical, and Visible Fluorescence Traits of Dy3+-doped SrGdGa3O7 Crystal
|
WANG Haidong, WANG Yan, ZHU Zhaojie, LI Jianfu, LAKSHMINARAYANA Gandham, TU Chaoyang
|
|
|
Table 6 Comparative spectral features of some Dy3+-doped crystals
|
|
Crystals | $\bar{\lambda}$/nm | FWHM/nm | σem/(×10-21, cm2) | τr/ms | τf/ms | η/% | Ref. | Dy:LiNbO3 | 575 | - | 3.2 (π) 0.3 (σ) | 0.292 | 0.268 | 91.8 | [35] | Dy:YAG | 583 | - | 2.09 | 1.02 | 0.4 | 39.2 | [23] | Dy: CaYAlO4 | 580 | - | 2.8 (π) 3.6 (σ) | 0.485 | 0.262 | 54.0 | [21] | Dy:CaGdAlO4 | 578 | 13(π) 14 (σ) | 0.55 (π) 0.51 (σ) | 0.501 | 0.222 | 44.3 | [22] | Dy:Sr3Y(BO3)3 | 576 | 16 (σ) 17 (π) | 1.0 (σ) 1.2 (π) | 1.45 | 0.820 | 56.6 | [28] | Dy: CNGS | 572 | 16.3 (σ) 15.8 (π) | 1.35 (σ) 1.89 (π) | 1.22 | 0.293 | 26.5 | [27] | Dy:GGG | 581 | - | 2.62 | 1.107 | 0.79 | 71.4 | [31] | Dy:SGGM | 574 | 15.6(π) 16.2(σ) | 1.84 (π) 2.49 (σ) | 0.768 | 0.531 | 69.1 | This work |
|
|
|