Dy3+掺杂SrGdGa3O7晶体的晶体生长, 结构、光学和可见光荧光特性
|
王海东, 王燕, 朱昭捷, 李坚富, LAKSHMINARAYANA Gandham, 涂朝阳
|
Crystal Growth and Structural, Optical, and Visible Fluorescence Traits of Dy3+-doped SrGdGa3O7 Crystal
|
WANG Haidong, WANG Yan, ZHU Zhaojie, LI Jianfu, LAKSHMINARAYANA Gandham, TU Chaoyang
|
|
|
Table 4 Comparison of J-O intensity parameters with other Dy3+-doped materials
|
|
Crystal | Ω2/(×10-20, cm2) | Ω4/(×10-20, cm2) | Ω6/(×10-20, cm2) | Ref. | Dy: LiLuF4 | 2.04 | 0.91 | 1.09 | [34] | Dy: YAG | 1.49 | 0.94 | 3.20 | [23] | Dy: CaGdAlO4 | 1.80 | 1.00 | 0.50 | [22] | Dy: CaYAlO4 | 5.05 | 9.95 | 3.12 | [21] | Dy: Sr3Y(BO3)3 | 2.39 | 0.88 | 1.22 | [28] | Dy: LiNbO3 | 5.42 | 1.14 | 2.51 | [35] | Dy: YSGG | 0.13 | 0.73 | 1.06 | [36] | Dy: GGG | 0.17 | 2.66 | 2.57 | [31] | Dy: SGGM | 5.113 (π) 5.686 (σ) 5.495 (eff) | 1.796 (π) 1.316 (σ) 1.476 (eff) | 0.843 (π) 1.243 (σ) 1.110 (eff) | This work |
|
|
|