Dy3+掺杂SrGdGa3O7晶体的晶体生长, 结构、光学和可见光荧光特性
|
王海东, 王燕, 朱昭捷, 李坚富, LAKSHMINARAYANA Gandham, 涂朝阳
|
Crystal Growth and Structural, Optical, and Visible Fluorescence Traits of Dy3+-doped SrGdGa3O7 Crystal
|
WANG Haidong, WANG Yan, ZHU Zhaojie, LI Jianfu, LAKSHMINARAYANA Gandham, TU Chaoyang
|
|
|
Table 3 Experimental and calculated line strengths in Dy:SGGM crystal
|
|
Transition 6H15/2→ | π-polarization | σ-polarization | $\bar{\lambda}$/nm | Sexp/(×10-20, cm2) | Scalc/(×10-20, cm2) | $\bar{\lambda}$/nm | Sexp/(×10-20, cm2) | Scalc/(×10-20, cm2) | 4G11/2 | 426 | 0.053 | 0.028 | 422 | 0.076 | 0.022 | 4I15/2 | 450 | 0.104 | 0.093 | 450 | 0.148 | 0.123 | 4F9/2 | 470 | 0.039 | 0.033 | 473 | 0.055 | 0.043 | 6F3/2 | 766 | 0.088 | 0.051 | 761 | 0.077 | 0.076 | 6F5/2 | 791 | 0.286 | 0.291 | 792 | 0.403 | 0.429 | 6F7/2 | 893 | 0.978 | 0.846 | 901 | 1.179 | 1.067 | 6H7/2+6F9/2 | 1074 | 1.631 | 1.672 | 1079 | 1.677 | 1.701 | 6H9/2+6F11/2 | 1266 | 6.670 | 6.660 | 1259 | 6.961 | 6.953 | 6H11/2 | 1693 | 0.970 | 1.078 | 1656 | 1.292 | 1.370 | RMS/(×10-20, cm2) | | 0.074 | | | 0.063 | |
|
|
|