新型复合支撑体共烧制备致密La0.7Ca0.3Cr0.97O3-δ连接体薄膜
王松林1,2, 凤仪2, 王东生1, 孟广耀3

Fabrication of Dense La0.7Ca0.3Cr0.97O3-δ Interconnect Membrane on Novel SOFC Composite Support by Co-firing
WANG Song-Lin1,2, FENG Yi2, WANG Dong-Sheng1, MENG Guang-Yao3
图3 NiOLCC97复合材料在1400℃烧结4 h后的断面SEM照片
Fig. 3 SEM images of the fracture surfaces of the NiOLCC97 composites sintered at 1400℃ for 4 h a,b 5wt% NiO; c,d 50wt% NiO; e,f 75wt% NiO; a, c, e before reducing; b, d, f after reducing