新型复合支撑体共烧制备致密La0.7Ca0.3Cr0.97O3-<italic>δ</italic>连接体薄膜

新型复合支撑体共烧制备致密La_0.7Ca_0.3Cr_0.97O_3-_δ连接体薄膜

王松林^1,², 凤仪², 王东生¹, 孟广耀³

Fabrication of Dense La_0.7Ca_0.3Cr_0.97O_3-_δ Interconnect Membrane on Novel SOFC Composite Support by Co-firing

WANG Song-Lin^1,², FENG Yi², WANG Dong-Sheng¹, MENG Guang-Yao³

图2 NiOLCC97烧结样品的相对密度及还原后的孔隙率与NiO含量之间的关系
Fig. 2 Effect of NiO content on the relative densities of NiOLCC97 sintered samples and the porosity after reducing