Na2O-B2O3-SiO2玻璃焊料连接碳化硅陶瓷接口抗热震性能
Thermal Shock Behavior of the SiC-SiC Joints Joined with Na2O-B2O3-SiO2 Glass Solder
Fig. 5 Retained flexural strength of the SiCNBSSiC joints after different thermal cycles at a quenching temperature of 150℃
Na2O-B2O3-SiO2玻璃焊料连接碳化硅陶瓷接口抗热震性能 |
|
罗朝华 |
Thermal Shock Behavior of the SiC-SiC Joints Joined with Na2O-B2O3-SiO2 Glass Solder |
| 图5 SiCNBSSiC试条经150℃多次热震循环后残余弯曲强度 Fig. 5 Retained flexural strength of the SiCNBSSiC joints after different thermal cycles at a quenching temperature of 150℃ |
| |