Journal of Inorganic Materials
• Research Paper • Previous Articles Next Articles
WANG Yi-Lin; ZHAO Mei-Yu; WU Wen-Jun
Received:
Revised:
Published:
Online:
Abstract: The processing with a physical method by using combined-size particles to decrease firing temperature for Ni-Cu-Zn ferrite was reported. As the densification process can be accelerated by selecting suitable ratio of nano-particles and micro-particles, the firing temperature was decreased and high initial magnetic permeability was held above 700 for Ni0.13Cuo.26Zn0.64Fe1.9804 ferrite. The initial magnetic permeability of the low firing (900℃) ferrite prepared by combined-size powders with 10% nano-sized powders was 764.
Key words: soft ferrite, low sintering temperature, nano-particles
CLC Number:
TM271
WANG Yi-Lin,ZHAO Mei-Yu,WU Wen-Jun. High Permeability Ni-Cu-Zn Ferrite Prepared by Combined-size Particles Processing[J]. Journal of Inorganic Materials.
0 / / Recommend
Add to citation manager EndNote|Ris|BibTeX
URL: https://www.jim.org.cn/EN/
https://www.jim.org.cn/EN/Y2004/V19/I4/926