Microstructure and Property of MoSi2-30Al2O3 Electrothermal Coating Prepared by Atmospheric Plasma Spraying

doi:10.15541/jim20180394

Abstract

Abstract:

With MoSi₂-30Al₂O₃mixed powders as the raw material, MoSi₂-30Al₂O₃ electrothermal coating was sprayed by atmospheric plasma spraying technology. The phase composition, microstructure and thermal stability of the coating were systematically studied by XRD, SEM, electrical test and differential thermal gravity analysis. The results show that MoSi₂-30Al₂O₃ electrothermal coating shows dense microstructure. Al₂O₃ can improve the electrical resistivity and oxidation resistance of MoSi₂materials in low temperature. The coating exhibits an excellent electrical-heating performance. In the heating cycle test, it could be heated to 320 ℃ stably and exhibit uniform thermal distribution in the surface area. The temperature variation in roll’s central area can be controlled within 25 ℃; Oxidation and thermal stress relaxation during heating cycle would generate cracks and pores in the coating which would increase electrical resistivity.

Key words: electrothermal material, MoSi₂-Al₂O₃composite coating, atmospheric plasma spraying, electrical- heating performance

CLC Number:

TQ174

Yan-Zhe ZHOU, Min LIU, Kun YANG, Wei ZENG, Jin-Bing SONG, Chun-Ming DENG, Chang-Guang DENG. Microstructure and Property of MoSi₂-30Al₂O₃ Electrothermal Coating Prepared by Atmospheric Plasma Spraying[J]. Journal of Inorganic Materials, 2019, 34(6): 646-652.

Figures/Tables 13

Table 1 Atmospheric plasma spraying parameters

Sample	Current/A	Voltage/V	Distance/mm	Flux of Ar/(L?min^-1)	Flux of H₂/(L?min^-1)	Powder feed rate/(g?min^-1)
NiAl	600	70	110	45	8	20
MgAl₂O₄	630	75	110	40	11	19
MoSi-Al₂O₃	600	76	110	41	12	24

Fig. 1 XRD patterns of MoSi2-30Al2O3 powder and coating

Fig. 2 SEM images of MoSi2-30Al2O3 coating

Fig. 3 Polished cross-section morphologies of electrothermal coating system (a) and MoSi2-30Al2O3 coating (b, c); EDS analysis of corresponding points (1,2,3)

Fig. 4 Thermogravimetric (TG) curves of MoSi2-Al2O3 coating

Fig. 5 Thermogravimetric (TG) and differential scanning calorimeter (DSC) curves for MoSi2-30Al2O3 coating

Fig. 6 Photograph of ceramic heating roller (a) and infrared thermal image of the heating roller during insulation stage (b)

Fig. 7 Heating t-T curves of MoSi2-Al2O3 heating roller

Fig. 8 Cyclic heating t-T curve of MoSi2-30Al2O3 heating roller

Fig. 9 Relationship between resistivity of coating and heating time

Fig. 10 Relationship between resistivity of coating and temperature

Fig. 11 XRD pattern of MoSi2-30Al2O3 coating after 5 heating cycles

Fig. 12 Surface (a), cross-section (b) and fracture (c) morphologies of MoSi2-30Al2O3 coating after 5 cycles; EDS analysis of corresponding point (1)

References 22

[1]	PRUDENZIATI M . Development and the implementation of high-temperature reliable heaters in plasma spray technology. Journal of Thermal Spray Technology, 2008,17(2):234-243. DOI URL
[2]	GADOW R, KILLINGER A, LI C . Product development with thermally sprayed functional coatings on glass and glass-ceramics substrates. International Journal of Applied Ceramic Technology, 2005,2(6):493-503. DOI URL
[3]	PRUDENZIATI M, GUALTIERI M L . Electrical properties of thermally sprayed Ni- and Ni₂₀Cr-based resistors. Journal of Thermal Spray Technology, 2008,17(3):385-394. DOI URL
[4]	CHANG C, CHEN C Z, SUN W C , et al. Microstructure and electrothermal properties of SiC/55MoSi₂ materials. Journal of Silicate, 2003,231:862-866.
[5]	SCHEITZ S, TOMA F L, BERGER L M , et al. Thermisch gespritzte keramische Schichtheizelemente. Thermally Sprayed Multilayer Ceramic Heating Elements, 2011,4:88-92.
[6]	ZHANG Y, LI Y, BAI C . Microstructure and oxidation behavior of Si-MoSi₂ functionally graded coating on Mo substrate. Ceramics International, 2017,43(8):6250-6256. DOI URL
[7]	FENG P Z, QU X H . Progress in the research and application of MoSi₂ heating element. China Molybdenum Indusry, 2005,29(2):38-42.
[8]	BERZTISS D A, CERCHIARA R R, GULBRANSEN E A , et al. Oxidation of MoSi₂ and comparison with other silicide materials. Materials Science & Engineering A, 1992,155(1/2):165-181.
[9]	CHOU T C, NIEH T G . Mechanism of MoSi₂ pest during low temperature oxidation. Journal of Materials Research, 1993,8(1):214-226. DOI URL
[10]	FEI X, NIU Y, JI H , et al. Oxidation behavior of Al₂O₃ reinforced MoSi₂ composite coatings fabricated by vacuum plasma spraying. Ceramics International, 2010,36:2235-2239. DOI URL
[11]	HUANG H H, LIU Y S, CHEN Y M , et al. Effect of oxygen pressure on the microstructure and properties of the Al₂O₃-SiO₂ thin films deposited by E-beam evaporation. Surface & Coatings Technology, 2006,200(10):3309-3313.
[12]	KÖBEL S, PLÜSCHKE J, VOGT U , et al. MoSi₂-Al₂O₃ electroconductive ceramic composites. Ceramics International, 2004,30(8):2105-2110. DOI URL
[13]	TOMA F L, SCHEITZ S, BERGER L M , et al. Comparative study of the electrical properties and characteristics of thermally sprayed alumina and spinel coatings. Journal of Thermal Spray Technology, 2011,20(1/2):195-204. DOI URL
[14]	MAO J Y, LIU M, MAO J , et al. Oxidation-resistance of ZrB₂-MoSi₂ composite coatings prepared by atmospheric plasma spraying. Journal of Inorganic Materials, 2015,30(3):282-286. DOI URL
[15]	WANG L, FU Q, ZHAO F . Improving oxidation resistance of MoSi₂ coating by reinforced with Al₂O₃ whiskers. Intermetallics, 2018,94:106-113. DOI URL
[16]	LIU X Z, DENG C M, DENG C G , et al. Mullite-modified ZrB₂-MoSi₂ coating for carbon/carbon composites to withstand long term ablation. Ceramics International, 2017,44(4):4330-4337.
[17]	NEWMAN A, SAMPATH S, HERMAN H . Processing and properties of MoSi₂-SiC and MoSi₂-Al₂O₃. Materials Science & Engineering A, 1999,261(1/2):252-260.
[18]	WANG D Z, LIU X Y, ZUO T Y . MoSi₂-Mo₅Si₃ low temperature behavior of MoSi₂-Mo₅Si₃ composites. Journal of Rare Metal materials and Engineering, 2002,31(1):48-51.
[19]	ZHOU H M, LIU G Q, XIAO L R , et al. Low temperature oxidation behavior of MoSi₂ composeties strengthened and toughened by Si₃N₄ particles and SiC whiskers. Journal of Inorganic Materials, 2009,24(5):929-933. DOI URL
[20]	MESCHTER P J . Oxidation of MoSi₂/TiB₂ and MoSi₂/Al₂O₃ mixtures. Scripta Metallurgica Et Materialia, 1991,25(5):1065-1069. DOI URL
[21]	MARUYAMA T, YANAGIHARA MK . High temperature oxidation and pesting ofo(Si,A)₂. Materials Science & Engineering A, 1997, 239-240:828-841.
[22]	WANG G, ZHAO S K, JIANG W . Progress in the low temperature oxidation of MoSi₂. Journal of Inorganic Materials, 2001,16(6):1041-1048.

Microstructure and Property of MoSi₂-30Al₂O₃ Electrothermal Coating Prepared by Atmospheric Plasma Spraying

RichHTML

PDF (PC)

Knowledge

Cited

Abstract

Cite this article

share this article

Figures/Tables 13

References 22

Related Articles 4

Recommended Articles

Metrics

Comments

[1]	LI Da-Chuan, ZHAO Hua-Yu, ZHONG Xing-Hua, TAO Shun-Yan. Research Progresses of Atmospheric Plasma Sprayed Splat [J]. Journal of Inorganic Materials, 2017, 32(6): 571-580.
[2]	SUN Xu-Xuan, CHEN Hong-Fei, YANG Guang, LIU Bin, GAO Yan-Feng. YSZ- Ti₃AlC₂ Thermal Barrier Coating and Its Self-healing Behavior under High Temperatures [J]. Journal of Inorganic Materials, 2017, 32(12): 1269-1274.
[3]	YU Fang-Li, BAI Yu, WU Xiu-Ying, Wang Hai-Jun, WU Jiu-Hui. Corrosion Resistance and Anti-wear Property of Nickel Based Abradable Sealing Coating Deposited by Plasma Spraying [J]. Journal of Inorganic Materials, 2016, 31(7): 687-693.
[4]	MAO Jin-Yuan, LIU Min, MAO Jie, DENG Chun-Min, ZENG De-Chang, XU Lin. Oxidation-resistance of ZrB₂-MoSi₂ Composite Coatings Prepared by Atmospheric Plasma Spraying [J]. Journal of Inorganic Materials, 2015, 30(3): 282-286.