Synthesis of Porous g-C3N4 Loaded With Highly Dispersed PANI by Interfacial Polymerization and Its Photocatalytic Performance

doi:10.15541/jim20150092

Abstract

Abstract:

Polyaniline (PANI) was successfully loaded on porous graphitic carbon nitride (porous g-C₃N₄) by interfacial polymerization of aniline monomers. The structure, morphology and properties of the prepared samples were characterized by XRD, FTIR, SEM, TGA, UV-Vis and Electrochemical Impedance Spectroscope (EIS). Photocatalytic degradation of methylene blue was investigated to determine the photoactivity of the catalyst. The porous g-C₃N₄ showed good dispersion and interfacial adhesion to PANI, which improved the photocatalytic degradation of methylene blue and thermal stability. The improved photocatalytic activity could be attributed to the improved visible light utilization, oxidation power and electron transport property.

Key words: porous g-C3N4, PANI, thermal stability, interfacial polymerization, photocatalytic performance

CLC Number:

TQ174

LI Xian-Hua, ZHANG Lei-Gang, WANG Xue-Xue, YU Qing-Bo. Synthesis of Porous g-C₃N₄ Loaded With Highly Dispersed PANI by Interfacial Polymerization and Its Photocatalytic Performance[J]. Journal of Inorganic Materials, 2015, 30(10): 1018-1024.

Figures/Tables 7

Fig. 1 Adsorption of samples under dark conditions

Fig. 2 (a) XRD, (b) FTIR spectra and (c) nitrogen adsorption-desorption isotherms of porous g-C3N4 (1), PANI (2), and the porous g-C3N4/PANI composite (3)

Fig. 3 Typical SEM images of porous g-C3N4 at (high (a) and low (d) magnification), PANI (b), and the porous g-C3N4/PANI composite at (high (b) and low (e) magnification)

Fig. 4 Schematic presentation for fabrication of porous g-C3N4/PANI composite

Fig. 5 (a) TGA curves, (b) UV-Vis absorption spectrum, (c) plots of (αhν)2 vs photon energy (hν) for the band gap energy, and (d) Mott-Schottky plots for PANI nanorods (1), porous g-C3N4/PANI composite (2), and porous g-C3N4 (3)

Fig. 6 Photocurrent densities (a) and EIS spectra (b) of porous g-C3N4/PANI composite (1) and porous g-C3N4 (2)

Fig. 7 Photocatalytic effect of the samples process of photocatalytic degradation of MB under visible light irradiation (λ>400 nm), (b) first-order plots for the photodegradation of MB, (c) recycle test of porous g-C3N4/PANI composite catalyst, and (d) photocatalytic degradation of MB in the presence of different ratio of porous g-C3N4/PANI

References 18

[1]	WANG X, MAEDA K, THOMAS A, et al.A metal-free polymeric photocatalyst for hydrogen production from water under visible light.Nat. Mater., 2009, 8(1): 76-80.
[2]	ZHAN YJ, MORI T, NIU L, et al.Non-covalent doping of graphitic carbon nitride polymer with graphene: controlled electronic structure and enhanced optoelectronic conversion. Energ. Environ. Sci., 2011, 4(11): 4517-4521.
[3]	ZHANG XD, XIE X, WANG H.Enhanced photoresponsive ultrathin graphitic-phase C3N4 nanosheets for bioimaging.J. Am. Chem. Soc., 2012, 135(1): 18-21.
[4]	WANG XC, CHEN XF, THOMAS A, et al.Metal-containing carbon nitride compounds: a new functional organic-metal hybrid material.Adv. Mater., 2009, 21(16): 1609-1612.
[5]	WANG YJ, SHI R, LIN J, et al.Enhancement of photocurrent and photocatalytic activity of ZnO hybridized with graphite-like C3N4.Energ. Environ. Sci., 2011, 4(8): 2922-2929.
[6]	ZHANG S, ZHAO L, ZENG M, et al.Hierarchical nanocomposites of polyaniline nanorods arrays on graphitic carbon nitride sheets with synergistic effect forphotocatalysis.Catal. Today, 2014, 224(4): 114-121.
[7]	GE L, HAN C, LIU J.In situ synthesis and enhanced visible light photocatalytic activities of novel PANI-g-C3N4 composite photocatalysts. J. Mater. Chem., 2012, 22(23): 11843-11850.
[8]	HU HAI-XIAN, YUAN CHANG-SONG, CHEN XIANG-YANG.Study on the thermal performance of a bicomponent high performance epoxy resin for advanced composites. Journal of Anhui University of Science and Technology (Natural Science), 2012, 34(1): 39-42.
[9]	YU Q, LI X, ZHANG M.One-step fabrication and high photocatalytic activity of porous graphitic carbon nitride synthesised via direct polymerisation of dicyandiamide without templates. Micro Nano Lett., 2014, 9(1): 1-5.
[10]	POUGET J P, JOZEFOWICZ M E, EPSTEIN A J, et al.X-ray structure of polyaniline.Macromolecules, 1991, 24(3): 779-789.
[11]	RAFIEE M A, RAFIEE J, WANG Z, et al.Enhanced mechanical properties of nanocomposites at low graphene content.ACS Nano, 2009, 3(12): 3884-3890.
[12]	YAN J, WEI T, SHAO B, et al.Preparation of a grapheme nanosheet/polyaniline composite with high specific capacitance.Carbon, 2012, 48(2): 487-493.
[13]	XU J J, WANG K, ZU S Z, et al.Nanocomposites of polyaniline nanowire arrays on graphene oxide sheets with synergistic effect for energy storage.ACS Nano, 2010, 4(9): 5019-5026.
[14]	AFZAL A B, AKHTAR M J, NADEEM M, et al.Investigation of structural and electrical properties of polyaniline/gold nanocomposites. J. Phys. Chem. C, 2009, 113(40): 17560-17565.
[15]	KIM H, ABDALA A A, MACOSKO C W.Graphene/polymer nanocomposites.Macromolecules, 2010, 43(16): 6515-6530.
[16]	BAO C, GUO Y, SONG L, et al.Poly(vinyl alcohol) nanocomposites based on graphene and graphite oxide: a comparative investigation of property and mechanism.J. Mater. Chem., 2011, 21(36): 13942-13950.
[17]	WANG W, ZHONG Q X.Improved thermal stability of whey protein-maltodextrin conjugates at pH 5.0 by D-Glucose, sucrose, D-cellobiose, and lactose. Food Hydrocolloids, 2014, 41(12): 257-264.
[18]	HOU Y, ZUO F, DAGG A, et al.A three-dimensional branched cobalt-doped а-Fe2O3 nanorod/MgFe2O4 heterojunction array as a flexible photoanode for efficient photoelectrochemical water oxidation. Angew. Chem. Int. Ed., 2013, 52(4): 1248-1252.

Synthesis of Porous g-C₃N₄ Loaded With Highly Dispersed PANI by Interfacial Polymerization and Its Photocatalytic Performance

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 7

References 18

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	LI Yue, ZHANG Xuliang, JING Fangli, HU Zhanggui, WU Yicheng. Growth and Property of Ce³⁺-doped La₂CaB₁₀O₁₉ Crystal [J]. Journal of Inorganic Materials, 2023, 38(5): 583-588.
[2]	ZHAO Yupeng,HE Yong,ZHANG Min,SHI Junjie. First-principles Study on the Photocatalytic Hydrogen Production of a Novel Two-dimensional Zr₂CO₂/InS Heterostructure [J]. Journal of Inorganic Materials, 2020, 35(9): 993-998.
[3]	JIANG Hai-Yan, XIA Yun-Sheng, LI Yu-Zhen. Preparation and Visible-light-driven Photocatalytic Performance of Porous Rod-like FeVO₄ [J]. Journal of Inorganic Materials, 2018, 33(9): 949-955.
[4]	LIU Ding, YU Yang, MI Le, YU Yun, SONG Li-Xin. Preparation of Room Temperature Curable Organic-inorganic Hybrid Thermal Control Coatings [J]. Journal of Inorganic Materials, 2018, 33(8): 914-918.
[5]	FAN Guang-Xin, LIU Ze-Ping, WEN Yin, LIU Bao-Zhong. Surface Treatment on Structure and Property of LiNi_0.8Co_0.15Al_0.05O₂ by Silane Coupling Agent [J]. Journal of Inorganic Materials, 2018, 33(7): 749-755.
[6]	YANG Jing-Feng, WANG Qi-Hua, WANG Ting-Mei. Synthesis and Property of Alumina Aerogel [J]. Journal of Inorganic Materials, 2018, 33(3): 259-265.
[7]	ZHANG Heng-Fei, LIU Wei, LEI Jiao-Jiao, SONG Hua-Ting, QI Hong. Pd Doping on H₂/CO₂ Separation Performance and Hydrothermal Stability of Organic-inorganic Hybrid SiO₂ Membranes [J]. Journal of Inorganic Materials, 2018, 33(12): 1316-1322.
[8]	WANG Mi-Tang, FANG Long, LI Mei, LIU Zhao-Gang, HU Yan-Hong, ZHANG Xiao-Wei. Effect of Rare Earth Dopant on Thermal Stability and Structure of ZnO-B₂O₃-SiO₂ Glass [J]. Journal of Inorganic Materials, 2017, 32(6): 643-648.
[9]	LONG Pei-Qing, LIU Xi-Tao, YI Zhi-Guo. Effect of Sintering Process on Microstructure and Properties of Ba_0.85Ca_0.15)(Ti_0.9Zr_0.1)O₃Lead-free Ceramics [J]. Journal of Inorganic Materials, 2017, 32(3): 299-304.
[10]	WANG Nai-Qian, ZHANG Qun, SHIEH Han-Ping. Influence of Double Channel Layers on the Performance of Nitrogen Doped Indium-zinc-oxide Thin Film Transistors [J]. Journal of Inorganic Materials, 2016, 31(7): 745-750.
[11]	XIE Xiao-Hua, LI Xiao-Zhe, LI Wei-Biao, SHAO Guang-Jie, XIA Bao-Jia. Fabrication and Performance of PET-ceramic Separators [J]. Journal of Inorganic Materials, 2016, 31(12): 1301-1305.
[12]	LUO Ling-Hong, YU Hui, HUANG Zu-Zhi. Research Progress of the Sealing Glass for Intermediate Temperature Solid Oxide Fuel Cell [J]. Journal of Inorganic Materials, 2015, 30(2): 113-121.
[13]	LI Jia-Ke, LIU Xin, HUANG LI-Qun, WANG Yan-Xiang. LaFe_1-_xMg_xO₃ Ultrafine Powders Synthesized by Solution Combustion and Its Photocatalytic Performances [J]. Journal of Inorganic Materials, 2015, 30(11): 1223-1227.
[14]	CHEN Chen, ZHANG Hai-Bin, PENG Shu-Min, ZHAO Lin-Jie, ZHU Jian-Guo. High Temperature Hydrogenation Behavior of Bulk Titanium Aluminum Carbide [J]. Journal of Inorganic Materials, 2014, 29(8): 864-868.
[15]	YIN Dong-Mei, TU De-Yang, CHE Bing-Chen, ZHANG Fang-Fang, LIN Chang-Gui, DAI Shi-Xun. Effect of Sn Addition on the Structure and Optical Properties of Ge-Se-Te Chalcogenide Glasses [J]. Journal of Inorganic Materials, 2014, 29(3): 279-283.