Synthesis and Visible-light Photocatalytic Activities of Bi2Sn2O7

doi:10.15541/jim20140236

Abstract

Abstract:

Bi₂Sn₂O₇ photocatalysts with rods and microspheres composed of particles were successfully synthesized via a facile hydrothermal route. Adding order change of the raw materials resulted in different forms of nucleation, thus affected the final morphology of the products. The as-prepared Bi₂Sn₂O₇ was a special kind of complex oxide with pyrochlore structure, which possessed visible photocatalytic performance with the band gap of 2.61 eV. Photocatalytic activities of the products were evaluated by degradation of RhB under visible light. Bi₂Sn₂O₇ exhibited high Photocatalytic activities with degradation rate of 98% within 100 min. Particularly, microsphere shaped Bi₂Sn₂O₇ composed of particles possessed higher photocatalytic activities. Under condition of different free radicals quenchers, ·O₂^- and h⁺ were recognized as primary active species responsible for RhB degradation.

Key words: Bi2Sn2O7, visible light, hydrothermal synthesis, photocatalysis

CLC Number:

O643

GAO Er-Ping, WANG Wen-Zhong. Synthesis and Visible-light Photocatalytic Activities of Bi₂Sn₂O₇[J]. Journal of Inorganic Materials, 2015, 30(1): 87-92.

Figures/Tables 6

Fig. 1 XRD patterns of as-prepared Bi2Sn2O7-particle and Bi2Sn2O7-rod samples

Fig. 2 UV-visible diffuse reflectance spectra of γ-Bi2Sn2O7 products. Inset: plots of (αhυ)2 versus photon energy (hυ)

Fig. 3 SEM images of Bi2Sn2O7-rod samples (a and b) and Bi2Sn2O7-particle samples (c and d)

Fig. 4 Photocatalytic degradation of RhB as a function of irradiation time by different photocatalysts

Fig. 5 Effect of different scavengers on the photocatalytic degradation of RhB

Fig. 6 Schematic structure of Bi2Sn2O7 (a), diagrammatic representation of Bi3+ cation environments (b), coordination environment around Bi atom (c) and coordination environment around Sn atom (d)

References 23

[1]	KUDO A, OMORI K, KATO H.A novel aqueous process for preparation of crystal form-controlled and highly crystalline BiVO4 powder from layered vanadates at room temperature and its photocatalytic and photophysical properties.J. Am. Chem. Soc., 1999, 121(49): 11459-11467.
[2]	ZHANG C, ZHU Y.Synthesis of square Bi2WO6 nanoplates as high-activity visible-light-driven photocatalysts.Chem. Mater., 2005, 17(13): 3537-3545.
[3]	SHIMODAIRA Y, KATO H, KOBAYASHI H, et al.Photophysical properties and photocatalytic activities of bismuth molybdates under visible light irradiation.J. Phys. Chem. B, 2006, 110(36): 17790-17797.
[4]	PAN C, ZHU Y.New type of BiPO4 oxy-acid salt photocatalyst with high photocatalytic activity on degradation of dye.Environ. Sci. Technol., 2010, 44(14): 5570-5574.
[5]	YAO W F, WANG H, XU X H, et al.Photocatalytic property of bismuth titanate Bi2Ti2O7.Appl. Catal. A: Gen., 2004, 259(1): 29-33.
[6]	KUDO A, KATO H, TSUJI I.Strategies for the development of visible-light-driven photocatalysts for water splitting.Chem. Lett., 2004, 33(12): 1534-1539.
[7]	STOLTZFUS M W, WOODWARD P M, SESHADRI R, et al.Structure and bonding in SnWO4, PbWO4, and BiVO4: lone pairs vs inert pairs. Inorg. Chem., 2007, 46(10): 3839-3850.
[8]	WALSH A, WATSON G W, PAYNE D J, et al.A theoretical and experimental study of the distorted pyrochlore Bi2Sn2O7.J. Mater. Chem., 2006, 16(34): 3452-3458.
[9]	TOKUNAGA S, KATO H, KUDO A.Selective preparation of monoclinic and tetragonal BiVO4 with scheelite structure and their photocatalytic properties.Chem. Mater., 2001, 13(12): 4624-4628.
[10]	KE D, PENG T, MA L, et al.Effects of hydrothermal temperature on the microstructures of BiVO4 and its photocatalytic O2 evolution activity under visible light.Inorg. Chem., 2009, 48(11): 4685-4691.
[11]	ZHANG X, AI Z, JIA F, et al.Selective synthesis and visible-light photocatalytic activities of BiVO4 with different crystalline phases.Mater. Chem. Phys., 2007, 103(1): 162-167.
[12]	WALSH A, YAN Y, HUDA M N, et al.Band edge electronic structure of BiVO4: elucidating the role of the Bi s and V d orbitals.Chem. Mater., 2009, 21(3): 547-551.
[13]	LI K, WANG H, YAN H.Hydrothermal preparation and photocatalytic properties of Y2Sn2O7 nanocrystals.J. Mol. Catal. A: Chem., 2006, 249(1/2): 65-70.
[14]	LI K, WANG Y, WANG H, et al.Hydrothermal synthesis and photocatalytic properties of layered La2Ti2O7 nanosheets.Nanotechnology, 2006, 17(19): 4863-4867.
[15]	ZENG J, WANG H, ZHANG Y, et al.Hydrothermal synthesis and photocatalytic properties of pyrochlore La2Sn2O7 nanocubes. J. Phys. Chem. C, 2007, 111(32): 11879-11887.
[16]	ZHU X, ZHANG J, CHEN F.Study on visible light photocatalytic activity and mechanism of spherical Bi12TiO20 nanoparticles prepared by low-power hydrothermal method.Appl. Catal. B: Environ., 2011, 102(1/2): 316-322.
[17]	KUDO A, KATO H, NAKAGAWA S.Water splitting into H2 and O2 on new Sr2M2O7 (M=Nb and Ta) photocatalysts with layered perovskite structures: factors affecting the photocatalytic activity.J. Phys. Chem. B, 1999, 104(3): 571-575.
[18]	HINOJOSA B B, NINO J C, ASTHAGIRI A.First-principles study of cubic Bi pyrochlores.Phys. Rev. B, 2008, 77(10): 104123.
[19]	MURUGESAN S, HUDA M N, YAN Y, et al.Band-engineered bismuth titanate pyrochlores for visible light photocatalysis. J. Phys. Chem. C, 2010, 114(23): 10598-10605.
[20]	MOENS L, RUIZ P, DELMON B, et al.A simplified partial ionic charge model to evaluate the role played by bismuth pyrostannate in multiphase catalysts for the selective oxidation of isobutene to methacrolein.Appl. Catal. A: Gen., 2003, 249(2): 365-374.
[21]	WU J, HUANG F, LU X, et al.Improved visible-light photocatalysis of nano-Bi2Sn2O7 with dispersed s-bands.J. Mater. Chem., 2011, 21(11): 3872-3876.
[22]	WALSH A, WATSON G W.Polymorphism in bismuth stannate: a first-principles study.Chem. Mater., 2007, 19(21): 5158-5164.
[23]	ZHU H, JIN D, ZHU L, et al.A general hydrothermal route to synthesis of nanocrystalline lanthanide stannates: Ln2Sn2O7 (Ln=Y, La-Yb).J. Alloys Compd., 2008, 464(1/2): 508-513.

Synthesis and Visible-light Photocatalytic Activities of Bi₂Sn₂O₇

RichHTML

PDF (PC)

Knowledge

Cited

Abstract

Cite this article

share this article

Figures/Tables 6

References 23

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	WU Lin, HU Minglei, WANG Liping, HUANG Shaomeng, ZHOU Xiangyuan. Preparation of TiHAP@g-C₃N₄ Heterojunction and Photocatalytic Degradation of Methyl Orange [J]. Journal of Inorganic Materials, 2023, 38(5): 503-510.
[2]	MA Xinquan, LI Xibao, CHEN Zhi, FENG Zhijun, HUANG Juntong. BiOBr/ZnMoO₄ Step-scheme Heterojunction: Construction and Photocatalytic Degradation Properties [J]. Journal of Inorganic Materials, 2023, 38(1): 62-70.
[3]	CHEN Hanxiang, ZHOU Min, MO Zhao, YI Jianjian, LI Huaming, XU Hui. 0D/2D CoN/g-C₃N₄ Composites: Structure and Photocatalytic Performance for Hydrogen Production [J]. Journal of Inorganic Materials, 2022, 37(9): 1001-1008.
[4]	XUE Hongyun, WANG Congyu, MAHMOOD Asad, YU Jiajun, WANG Yan, XIE Xiaofeng, SUN Jing. Two-dimensional g-C₃N₄ Compositing with Ag-TiO₂ as Deactivation Resistant Photocatalyst for Degradation of Gaseous Acetaldehyde [J]. Journal of Inorganic Materials, 2022, 37(8): 865-872.
[5]	CHI Congcong, QU Panpan, REN Chaonan, XU Xin, BAI Feifei, ZHANG Danjie. Preparation of SiO₂@Ag@SiO₂@TiO₂ Core-shell Structure and Its Photocatalytic Degradation Property [J]. Journal of Inorganic Materials, 2022, 37(7): 750-756.
[6]	WANG Xiaojun, XU Wen, LIU Runlu, PAN Hui, ZHU Shenmin. Preparation and Properties of Ag@C₃N₄ Photocatalyst Supported by Hydrogel [J]. Journal of Inorganic Materials, 2022, 37(7): 731-740.
[7]	LIU Xuechen, ZENG Di, ZHOU Yuanyi, WANG Haipeng, ZHANG Ling, WANG Wenzhong. Selective Oxidation of Biomass over Modified Carbon Nitride Photocatalysts [J]. Journal of Inorganic Materials, 2022, 37(1): 38-44.
[8]	ZHANG Xian, ZHANG Ce, JIANG Wenjun, FENG Deqiang, YAO Wei. Synthesis, Electronic Structure and Visible Light Photocatalytic Performance of Quaternary BiMnVO₅ [J]. Journal of Inorganic Materials, 2022, 37(1): 58-64.
[9]	LIU Peng, WU Shimiao, WU Yunfeng, ZHANG Ning. Synthesis of Zn_0.4(CuGa)_0.3Ga₂S₄/CdS Photocatalyst for CO₂ Reduction [J]. Journal of Inorganic Materials, 2022, 37(1): 15-21.
[10]	WANG Luping, LU Zhanhui, WEI Xin, FANG Ming, WANG Xiangke. Application of Improved Grey Model in Photocatalytic Data Prediction [J]. Journal of Inorganic Materials, 2021, 36(8): 871-876.
[11]	AN Weijia, LI Jing, WANG Shuyao, HU Jinshan, LIN Zaiyuan, CUI Wenquan, LIU Li, XIE Jun, LIANG Yinghua. Fe(III)/rGO/Bi₂MoO₆ Composite Photocatalyst Preparation and Phenol Degradation by Photocatalytic Fenton Synergy [J]. Journal of Inorganic Materials, 2021, 36(6): 615-622.
[12]	XIAO Xiang, GUO Shaoke, DING Cheng, ZHANG Zhijie, HUANG Hairui, XU Jiayue. CsPbBr₃@TiO₂ Core-shell Structure Nanocomposite as Water Stable and Efficient Visible-light-driven Photocatalyst [J]. Journal of Inorganic Materials, 2021, 36(5): 507-512.
[13]	DONG Zhengming, LI Xiu, CHEN Chen, CAO Minghe, YI Zhiguo. Photostriction of NBT-BNT Ceramics [J]. Journal of Inorganic Materials, 2021, 36(3): 277-282.
[14]	XIONG Jinyan, LUO Qiang, ZHAO Kai, ZHANG Mengmeng, HAN Chao, CHENG Gang. Facilely Anchoring Cu nanoparticles on WO₃ Nanocubes for Enhanced Photocatalysis through Efficient Interface Charge Transfer [J]. Journal of Inorganic Materials, 2021, 36(3): 325-331.
[15]	WANG Tingting, SHI Shumei, LIU Chenyuan, ZHU Wancheng, ZHANG Heng. Synthesis of Hierarchical Porous Nickel Phyllosilicate Microspheres as Efficient Adsorbents for Removal of Basic Fuchsin [J]. Journal of Inorganic Materials, 2021, 36(12): 1330-1336.