Preparation by MOCVD and Microwave Absorbing Properties of CF@Fe

doi:10.3724/SP.J.1077.2013.13155

Abstract

Abstract: The CF@Fe composites were prepared by depositing precusor Fe(CO)₅ on carbon fiber (CF) to form continuous α-Fe film through metal organic chemical vapor deposition (MOCVD) process. The X-ray diffraction (XRD), scanning electron microscope (SEM) and a vector network analyzer were used to characterize the structure and electromagnetic properties of the powder and to study absorbing properties, The results showed that the film layer deposited on the surface of carbon fibers was pure α-Fe phase, at about 0.7 μm in thickness. After being deposited by consecutive α-Fe film, the CF electromagnetic properties changed significantly with the absorbing capacity being improved. By using electromagnetic parameters of the coaxial ring samples, the reflectance curves of the CF and CF@Fe coating at thickness of 2 mm were calculated, The curves showed that absorption peak of the samples deposited by the consecutive α-Fe film moved to the high frequency, the value of the minimum reflection peak reduced, and the bandwidth (less than -10 dB) increased 4.2 GHz.

Key words: carbonyl iron, metal organic chemical vapor deposition (MOCVD), carbon fiber, microwave absorb

CLC Number:

TB383
TM277

LIU Yuan, LIU Xiang-Xuan, CHEN Xin, WANG Xuan-Jun. Preparation by MOCVD and Microwave Absorbing Properties of CF@Fe[J]. Journal of Inorganic Materials, 2013, 28(12): 1328-1332.

References

[1] ZHOU Ming-Shan, SHEN Rui-Qi, XU Ming, et al. Preparation and millimeter wave attenuation properties of carbon fibers coated by barium ferrite. Chinese Journal of Inorganic Chemistry , 2009, 25(9): 1622-1626.

[2] WANG Zhen-Jun, LI Ke-Zhi, WANG Chuang, et al. Wave absorbing properties of carbonyl iron powder/carbon fiber reinforced cement-based composites.Journal of the Chinese Ceramic Society, 2011, 39(1): 69-74.

[3] Laukaitis A, Sinica M, Balevicius S. Investigation of electromnetic wave absorber based on carbon fiber reinforced aerated concrete using time-domain method. Acta Phys Polonica A, 2008,113(3): 1047-1050.

[4] LI Yan, QIAO Xiao-Jing, REN Guo-Qing, et al. Preparation and microwave absorbing properties NiCo/NiFe coated carbon fibers. Aerospace Materials & Technology, 2012, 42(3): 29-33.

[5] FU Dao, ZHANG Lei, SUN Wan-Chang, et al. Research on chemical plating ni on carbon surface. Material & Heat Treatment, 2012, 41(16): 158-159.

[6] GAO Jia-Cheng, TAN Zun, REN Fu-Zhong. Study on kinetics and technology of Ni electroless plating on carbon fibers. Journal of Functional Materials, 2011, 8(42): 1360-1363.

[7] Jin G P, Wang X L, Fu Y, et al. Preparation of tetraoxalyl ethylenediamine melamine resin grafted-carbon fibers for nano-nickel recovery from spent electroless nickel plating baths. Chemical Engineering Journal, 2012, 203: 440-446.

[8] Hua Z S, LiuY H, Yao G C, et al. Preparation and characterization of nickel-coated carbon fibers by electroplating. Journal of Materials Engineering and Performance, 2012, 21(3):324-330.

[9] Wang R, Wan Y Z, He F, et al. The synthesis of a new kind of magnetic coating on carbon fibers by electrodeposition. Applied Surface Science, 2012, 258(7): 3007-3011.

[10] Manasevit H M. Single-crystal gallium arsenide on insulating substrates. Applied Physics Letters, 1968, 12(4): 156-159.

[11] LI Z M, LI J P, JIANG H Y, et al. Effect of thermocouple position on temperature field in nitride MOCVD reactor. Journal of Crystal Growth, 2013, 368:29-34.

[12] XIE Wei, CHENG Hai-Feng, CHU Zeng-Yong, et al. Radar absorbing properties of light radar absorbing materials based on hollow-porous carbon fibers. Journal of Inorganic Materials, 2009, 24(2):320-324.

[13] YU Dong-Xiu. Preparation and electromagnetic characteristic of magnetic and conductive modified short carbon fibers. Journal of Inorganic Materials, 2010, 25(5):463-467.

[14] LU Rui-Tao, KANG Fei-Yu, WEI Jin-Quan, et al. Electromagnetic property of α-Fe filled carbon nanotubes. Journal of Inorganic Materials, 2008, 23(1):23-28.

[15] ZHANG Shu-Yuan, CAO Quan-Xi. Electromagnetic and microwave absorption performance of some transition metal doped La0.7Sr0.3Mn1?xTMxO3±δ(TM = Fe, Co or Ni). Materials Science and Engineering B, 2012, 177(8): 678-684.

[16] 刘顺华，刘军民，董星龙, 等. 电磁波屏蔽及吸波材料. 北京:化学工业出版社, 2007: 235.

[17] Yang Y, Xu C L, Xia Y X, et al. Synthesis and microwave absorption properties of FeCo nanoplates. Journal of Alloys and Compounds, 2010, 493(1/2):549-552.