Effects of Holding Time on Intergranular Phase and Mechanical Property of GPS Silicon Nitride Ceramics

Abstract

Abstract: The effect of holding time on intergranular phase and mechanical property of GPS silicon nitride ceramics was studied. Results show that the contents of intergranular oxygen and total grain boundary phase as well as the density of sintered samples have maximum values with increasing the holding time. Among the range of holding time in this research (0-90min), however, the room temperature strength of GPS silicon nitride ceramics increases with expanding the holding time.

Key words: silicon nitride, intergranular phase, GPS, holding time

CLC Number:

TQ174

DAI Jian-Qing,HUANG Yong,XIE Zhi-Peng,MA Tian,YANG Jin-Long,MA Jing-Tao. Effects of Holding Time on Intergranular Phase and Mechanical Property of GPS Silicon Nitride Ceramics[J]. Journal of Inorganic Materials.

References

[1] Greil P. Mater. Sci. Eng., 1989, A109: 27--35.
[2] Hoffmann M J. MRS Bull., 1995, (2): 28--32.
[3] Tien T-Y. In: Alper A M ed. Phase Diagrams in Advanced Ceramics (United Kingdom Edition, Academic Press Limited, 1995): 127--155.
[4] 许兴利. 凝胶注模氮化硅陶瓷的显微结构与性能(博士后出站报告). 北京：清华大学材料科学与工程系, 1999.
[5] Clarke D R, Thomas G. J. Am. Ceram. Soc., 1977, 60 (11--12): 491--495.
[6] Kleebe H-J, Hoffmann M J, Rühle M. Z. Metallkd., 1992, 83: 610--617.
[7] Kleebe H-J, Cinibulk M K, Cannon R M, et al. J. Am. Ceram. Soc., 1993, 76 (8): 1969--1977.
[8] Kleebe H-J, Bruley J, Rühle M. J. Euro. Ceram. Soc., 1994, 14, 1--11.
[9] Tanaka T, Kleebe H J, Cinibulk M K, et al. J. Am. Ceram. Soc., 1994, 77 (4): 911--914.
[10] Wang C-M, Pan X-Q, Hoffmann A J, et al. J. Am. Ceram. Soc., 1996, 79 (3): 788--792.
[11] Natansohn S, Pasto A E, Rourke W J. J. Am. Ceram. Soc., 1993, 76 (9): 2273--2284.
[12] 代建清. 氮化硅粉料的表面特性对水基浓悬浮体制备和烧结体性能?的影响之研究(博士学位论文). 北京：清华大学材料科学与工程系, 2001.
[13] Dai J-Q, Huang Y, Xie Z-P, et al. “The effects of powder surfaces
modification and amount of oxide additives (Al₂O₃ and Y₂O₃) on rheological property of Si₃N₄ concentrated aqueous suspensions”, The Second
China International Conference on High-Performance Ceramics, Nov. 11-14, KunMing, China, 2001.
[14] Sato T, Tokunaga Y, Endo T, et al. J. Am. Ceram. Soc., 1988, 71 (12): 1074--1079.
[15] Standard methods for the examination of water and wastewater, 16^th ed. (the American Public Health Association, the American Water Works Association,
and the Water Pollution Control Council, New York, 1985): 382--383.
[16] Nakayasu T, Yamada T, Tanaka I, et al. J. Am. Ceram. Soc., 1998, 81 (3): 565--570.
[17] Stemmer S, Roebben S, Biest O V D. Acta Mater., 1998, 46 (15): 5599--5606.
[18] Wu Fengying, et al. Journal of Materials Science, 1994, 9 (3): 303--308.
[19] Bjorklund H, Falk L K L. J. Euro. Ceram. Soc., 1997, 17: 1301--1308.
[20] Sun E Y, Becher P F, Plucknett K P, et al. J. Am. Ceram. Soc., 1998, 81 (11): 2831--2840.
[21] Loehman R E. J. Am. Ceram. Soc., 1979, 62 (9--10): 491--494.
[22] Ekstrom T, Nygren M. J. Am. Ceram. Soc., 1992, 75 (2): 257--276.
[23] Pullum O J, Lewis M H. J. Euro. Ceram. Soc., 1996, 16: 1271--1275.
[24] Neidhardt U, Schubert H, Bischoff E, et al. Key Eng. Mater., 1994, 89-91: 187--192.
[25] 周龙捷. 碳化硅和氮化硅凝胶注模成型的研究(博士学位论文). 北京：清华大学材料科学与工程系, 2000.