MnOOH纳米棒的低温水热合成

doi:10.3724/SP.J.1077.2006.01249

无机材料学报

MnOOH纳米棒的低温水热合成

张元广^1,2, 陈友存¹

1. 安庆师范学院化学系, 安庆 246011; 2. 中国科学技术大学化学系, 合肥 230026

收稿日期:2005-08-03 修回日期:2005-12-05 出版日期:2006-09-20 网络出版日期:2006-09-20

Low-temperature Hydrothermal Synthesis of MnOOH Nanorods

ZHANG Yuan-Guang^1,2, CHEN You-Cun¹

1. Department of Chemistry, Anqing Teachers College, Anqing 246011, China; 2. Department of Chemistry, University of Science and Technology of China, Hefei 230026, China

Received:2005-08-03 Revised:2005-12-05 Published:2006-09-20 Online:2006-09-20

摘要/Abstract

摘要： 以KMnO₄和N₄(CH₂)₆为主要原料, 在130℃反应16h, 水热法制备了MnOOH纳米棒, 并利用X射线粉末衍射(XRD)、透射电子显微镜(TEM)和高分辨透射电子显微镜(HRTEM)等手段对产物进行了表征. 探索了KMnO₄和N₄(CH₂)₆间的摩尔比以及反应温度对合成产物的影响. 实验结果表明:产物为具有单斜结构的MnOOH纯相, 形貌为棒状, 呈现单晶特性.

关键词: MnOOH, 水热合成, 纳米棒

Abstract: MnOOH nanorods were synthesized hydrothermally at 130℃ for 16h, by using KMnO₄ and N₄(CH₂)₆ as main materials. The as-prepared samples were characterized by X-ray powder diffraction (XRD), transmission electron microscope (TEM), and high resolution transmission electron microscope (HRTEM). The effects of both molar ratios between reactants and reaction temperature on the products were investigated. The results show that the as-prepared MnOOH nanorods are with a monoclinic single phase, rod-like morphology and single crystalline nature.

Key words: MnOOH, hydrothermal synthesis, nanorodsenddocument

中图分类号:

O648
TB383

张元广,陈友存. MnOOH纳米棒的低温水热合成[J]. 无机材料学报, DOI: 10.3724/SP.J.1077.2006.01249.

ZHANG Yuan-Guang,CHEN You-Cun. Low-temperature Hydrothermal Synthesis of MnOOH Nanorods[J]. Journal of Inorganic Materials, DOI: 10.3724/SP.J.1077.2006.01249.

参考文献

[1] Kovtyukhova N I, Mallouk T E. Chem. Eur. J., 2002, 8: 4355--4359.
[2] Han W Q, Fan S S, Li Q Q, et al. Science, 1997, 277: 1287--1290.
[3] Martin R. Science, 1994, 266: 1961--1963.
[4] Pacholski C, Kornowski A, Weller H. Angew. Chem., 2002, 114: 1234--1239.
[5] Yang J, Xue C, Yu S H, et al. Angew. Chem., 2002, 114: 4891--4896.
[6] Bach S, Henry M, Baffier N, et al. J. Solid State Chem., 1990, 88: 325--329.
[7] Bach S, Pereira-Ramos J P, Baffier N, et al. Electrochim. Acta, 1991, 36: 1595--1599.
[8] Hunter J. J. Solid State Chem., 1981, 39: 142--145.
[9] Bach S, Pereira-Ramos J P, Baffier N. J. Solid State Chem., 1995, 120: 70--76.
[10] Al-Sagheer F A, Zaki, M I. Colloid Surface, 2000, A 173: 193--197.
[11] Cordoba de Torresi S I, Gorenstein A. Electrochim. Acta, 1992, 37: 2015--2018.
[12] Kanasaku T, Amezawa K, Yamamoto N. Solid State Ionics, 2000, 133: 51--56.
[13] Brock S L, Duan N, Rong T Z, et al. Chem. Mater., 1998, 10: 2619--2623.
[14] Wang X, Li Y D. Chem. Commun., 2002. 764--766.
[15] Wang X, Li Y D. J. Am. Chem. Soc., 2002, 124: 2881--2885.
[16] Xiong Y J, Xie Y. Chem. Eur. J. 2003, 9: 1645--1648.
[17] Wang W Z, Xu C K, Wang G H, et al. Adv. Mater., 2002, 14: 837--843.
[18] 张治安, 杨邦朝, 邓梅根, 等(ZHANG Zhi-An, et al). 无机?
材料学报(Journal of Inorganic Materials), 2005, 20 (3): 529--536.
[19] Shamma P K, Whittingham M S. Mater. Lett., 2001, 48: 319--313.
[20] Ocana M. Colloid Polyn. Sci., 2000, 278: 443--447.
[21] 朱归胜, 徐华蕊, 廖春图, 等 (ZHU Gui-Sheng, et al). 无
机材料学报(Journal of Inorganic Materials), 2005, 20 (2): 479--483.
[22] Zhang Y G, Liu Y, Guo F, et al. Solid State Commun., 2005, 134: 523--527.
[23] 董喜燕, 张兴堂, 程纲, 等(Dong Xi-Yian, et al).
化学学报(Acta Chimica Sinica), 2004, 62: 2441--2443.

MnOOH纳米棒的低温水热合成

Low-temperature Hydrothermal Synthesis of MnOOH Nanorods

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	吴爱军, 朱敏, 朱钰方. 含铜硅酸钙纳米棒复合水凝胶用于肿瘤治疗和皮肤伤口愈合性能研究[J]. 无机材料学报, 2022, 37(11): 1203-1216.
[2]	王婷婷, 史书梅, 柳晨媛, 朱万诚, 张恒. 多级多孔硅酸镍微球的合成及其对碱性品红的高效吸附[J]. 无机材料学报, 2021, 36(12): 1330-1336.
[3]	宋可可, 黄浩, 鲁梦婕, 杨安春, 翁杰, 段可. 水热制备锌、硅、镁、铁等元素掺杂羟基磷灰石及其表征[J]. 无机材料学报, 2021, 36(10): 1091-1096.
[4]	张东硕,蔡昊,高凯茵,马子川. Zn₂SiO₄-ZnO-生物炭复合物的制备及其可见光催化H₂O₂降解甲硝唑[J]. 无机材料学报, 2020, 35(8): 923-930.
[5]	朱泽阳,魏济时,黄健航,董向阳,张鹏,熊焕明. 晶格空位ZnO纳米棒的制备及其在镍锌电池中的应用[J]. 无机材料学报, 2020, 35(4): 423-430.
[6]	蒋海燕, 夏云生, 李育珍. 多孔棒状FeVO₄的制备及可见光催化性能研究[J]. 无机材料学报, 2018, 33(9): 949-955.
[7]	杜玉成, 王学凯, 侯瑞琴, 吴俊书, 张时豪, 祁超. 硅藻土原位生长Nb₂O₅纳米棒及表面Cr(VI)吸附转化行为研究[J]. 无机材料学报, 2018, 33(5): 557-564.
[8]	王树江, 杨永恒, 温春阳, 张国馗, 苑春晖. 纳米银/伊利石复合材料的制备及其性能研究[J]. 无机材料学报, 2018, 33(5): 570-576.
[9]	梁继然, 张叶, 杨然, 赵一瑞, 郭津榜. VO₂(B)/ZnO异质复合纳米棒结构的室温NH₃敏感性能研究[J]. 无机材料学报, 2018, 33(12): 1323-1329.
[10]	贾思齐, 蒋政, 迟莉娜, 叶瑛, 胡双双. 从天然辉锑矿中制备硫化锑纳米棒及其性能探究[J]. 无机材料学报, 2018, 33(11): 1213-1218.
[11]	吕玉珍, 孙倩,李超, 单秉亮, 齐波, 李成榕. 油酸修饰TiO₂纳米棒的溶剂热合成及形貌调控研究[J]. 无机材料学报, 2017, 32(7): 719-724.
[12]	郭宇, 李东昕, 吴红梅, 金玉家, 周立岱, 陈强强. 负载型TS-1沸石膜催化剂的制备、表征及其催化性能研究[J]. 无机材料学报, 2017, 32(6): 631-636.
[13]	Abubaker Abutartour, Lotfia El Majdoub, 史亚赛, 李妮丽, 徐庆红. 一种新型膦酸锆孔材料的合成及其对金属离子的吸附性质[J]. 无机材料学报, 2017, 32(3): 305-312.
[14]	高鑫, 刘祥萱, 朱左明, 谢拯, 佘兆斌. NiFe₂O₄/TiO₂纳米棒阵列薄膜光电化学性能和光催化性能研究[J]. 无机材料学报, 2016, 31(9): 935-942.
[15]	谢会东, 李飞, 陈超, 席海红, 史玲. 水热法合成陶瓷LaPO₄的微波介电性能[J]. 无机材料学报, 2015, 30(8): 882-886.