恒温环境中ZrB2氧化行为模拟

doi:10.15541/jim20180395

摘要/Abstract

摘要：

二硼化锆(ZrB₂)是一种应用于高超声速飞行器的新型防热材料, 近年来受到广泛关注。本研究根据ZrB₂在不同温度下的氧化产物二氧化锆(ZrO₂)与三氧化二硼(B₂O₃)的微观结构和形貌, 改进了原有的ZrB₂氧化唯象模型, 研究了ZrB₂的氧化行为, 提出了中等温度区间液态B₂O₃的生成、蒸发、填充的动态平衡关系, 并考虑了孔隙出口处的B₂O₃蒸气浓度。研究结果表明: 改进后的模型能够预测低流速准静态条件下ZrB₂的氧化行为, 与加热炉中的样品恒温氧化测试结果吻合良好; 孔隙对氧化过程有较大影响, 在相同的温度、氧分压下, 孔隙率越大, 被氧化程度越高; 在基材表面存在B₂O₃液态膜的情况下, 扩散过程对氧化速率的控制被极大地降低, 材料表现出最强的抗氧化性能。

关键词: 二硼化锆, 氧化行为, 孔隙率, 模拟, 液态膜

Abstract:

Zirconium diboride (ZrB₂), a thermal protection material for hypersonic vehicle, has received widespread attention in recent years. Here we advance an oxidation model based on oxidation products (ZrO₂and B₂O₃) and their morphology at different temperatures to simulate the oxidation behavior of ZrB₂. This study further establishes the dynamic equilibrium among formation, evaporation and supplement of B₂O₃ whose concentration at ambient was assumed to be nonzero. Research results indicate that the advanced model can predict the oxidation behavior of ZrB₂ under quasi-static low flow conditions and the simulation results are consistent with the data obtained from sample suspended in wire heater furnace at constant temperature. The porosity has a great influence on the oxidation process, and at the same temperature and oxygen partial pressure, the larger the porosity, the higher the oxidation degree. The oxidation rate controlled by diffusion in the presence of liquid B₂O₃film laying outer surface of substrate reduces greatly and the material exhibits the strongest oxidation resistance.

Key words: zirconium diboride, oxidation behavior, pore fraction, simulation, film

中图分类号:

周述光, 国义军, 刘骁. 恒温环境中ZrB₂氧化行为模拟[J]. 无机材料学报, 2019, 34(6): 660-666.

Shu-Guang ZHOU, Yi-Jun GUO, Xiao LIU. Simulation of ZrB₂ Oxidation Behavior at Constant Temperature Ambient[J]. Journal of Inorganic Materials, 2019, 34(6): 660-666.

图/表 4

图1 ZrB2氧化产物及其微观结构的示意图

Fig. 1 Schematic sketch of the oxidation products of ZrB2 and morphology assumed in the model L: scale thickness; Rs: recession of substrate; hext: outside layer thickness of B2O3; hint: inside layer thickness of B2O3; a: interface between ambient and oxide; zb: interface between liquid and inside solid; s: interface between oxides and substrate; i: interface between inside liquid and solid

图2 孔隙率对ZrB2氧化前后质量损失的影响

Fig. 2 Effect of pore fraction on weight change of ZrB2

图3 不同温度下ZrB2氧化前后质量变化模拟结果与测试结果的比较

Fig. 3 Comparison of mass change obtained from simulation results and sample measurement results of ZrB2 at different temperatures

表1 不同温度下氧化物B2O3与ZrO2的厚度比

Table 1 Ratio of thickness of B2O3 to that of ZrO2 at different temperatures

T/K	1098	1163	1263	1365	1478	1573	1673
Ratio	1.05	1.04	1.03	0.99	0.96	0.87	0.70

参考文献 30

[1]	CLOUGHERTY E V, KALISH D, PETER E T . esearch and development of refractory oxidation resistant diborides. RAFML-TR-68-190, 1968.
[2]	ZHANG GUO-JUN, LIU HAI-TAO, ZOU JI , et al. Chemical reactions in the life cycle of ZrB₂ ceramics. Chinese Science Bulletin, 2015,60(3):276-286. DOI URL
[3]	LI GANG, HAN WEN-BO, JIANG JIU-XING . Mechanicalproperties and thermal shock resistance of ZrB₂-SiC-AN ultrahigh temperature ceramics. Journal of Synthetic Crystals, 2009, 38, Special Edition: 36-39.
[4]	SONG JIAN-RONG, LI JUN-GUO, SHEN QIANG , et al. Thermal shock and oxidation resistances of ZrB₂-ZrO₂ ceramics. Journal of the Chinese Ceramic Society, 2008,36(5):663-667.
[5]	SONG JIE-GUANG, DU DA-MING, XU MING-HAN , et al. Oxidation behavior of ZrB₂-matrix composite materials at high-temperature conditions. Powder Metallurgy Technology, 2015,33(5):336-340, 364.
[6]	ZHOU HAI-JUN, ZHANG XIANG-YU, GAO LE , et al. Ablation properties of ZrB₂-SiC ultra-high temperature ceramic coatings. Journal of Inorganic Materials, 2013,28(3):256-260. DOI URL
[7]	ZHAO HAI-LEI, WANG JIAN, LI WEN-CHAO . Study on oxidation kinetics of ZrB₂-corundum-mullite composite. Naihuo Cailiao, 1998,32(6):322-325.
[8]	PARTHASARATHY T A, RAPP R A, OPEKA M , et al. A model for the oxidation of ZrB₂, HfB₂ and TiB₂. Acta Materialia, 2007,55(17):5999-6010. DOI URL
[9]	PARTHASARATHY T A, RAPP R A, OPEKA M , et al. A model for transitions in oxidation regimes of ZrB₂. Materials Science Forum, 2008. 595-598:823-832. DOI URL
[10]	PARTHASARATHY T A, RAPP R A, OPEKA M , et al. Effects of phase change and oxygen permeability in oxide scales on oxidation kinetics of ZrB₂ and HfB₂. Journal of the American Ceramic Society, 2009,92(5):1079-1086. DOI URL
[11]	BERKOWITZ-MATTUCK J B . High-temperature oxidation III. zirconium and hafnium diborides. Journal of the Electrochemical Society, 1966,113(9):908-914. DOI URL
[12]	HU PING, WANG GUO-LIN, WANG ZHI . Oxidation mechanism and resistance of ZrB₂-SiC composites. Corrosion Science, 2009,51(11):2747-2732.
[13]	ANDREEVA A F . Zirconium diboride low resistance layers. MAM’97-Materials for Advanced Metallization, Poster Session I, 1997.
[14]	PAGE R J, SHORT R A, HALBACH C R . Evaluation of zirconia, thoria and zirconium diboride for advanced resistojet use. NASA CR-112075, 1972.
[15]	MCCLAINE L A . Thermodynamic and kinetic studies for a refractory materials program, Part III. ASD-TDR-62-204Part III, 1964.
[16]	LUTHRA K L . Oxidation of carbon/carbon composites—a theoretical analysis. Carbon, 1988,26(2):217-224. DOI URL
[17]	. CHASE JR M W. , NIST-JANAF Thermochemical Tables 4 ^th Ed. Physical and Chemical Reference Data Monograph No.9, 1998: 286-291, 1756, 1780.
[18]	TRIPP W C, GRAHAM H C . Thermogravimetric study of the oxidation of ZrB₂ in the temperature range of 800 to 1500 ℃. Journal of the Electrochemical Society, 1971,118(7):1195-1199. DOI URL
[19]	PERRY R H, GREEN D W, MALONEY J O . Perry’s Chemical Engineers’ Handbook 7 ^th Ed. New York:McGraw-Hill, 1997: 570.
[20]	BARIN I . Thermochemical data of pure substances. New York: VCH Verlags-gesellschaft, 1995: 122-124.
[21]	JACOBSON N S, CURRY D M . Oxidation microstructure studies of reinforced carbon/carbon. Carbon, 2006,44(7):1142-1150. DOI URL
[22]	WELTY J R, RORRER G L, FOSTER D G . Fundamentals of momentum, heat and mass transfer 6th Ed. New York: WILEY, 2013,P448.
[23]	BIRD R B, STEWART W E, LIGHTFOOT E N . Transport phenomena. New York: John Wiley, 2002: 526, 866.
[24]	J. SZEKELY J, EVANS J, SOHN W H Y . Gas Solid Reactions. New York: Academic Press, 1976: 25.
[25]	DUFFA G. Ablative thermal protection system modeling . Reston: AIAA, Inc. Press, 2012: 109.
[26]	LI JIAN-FENG, ZHOU XIA-MING, DING CHUAN-XIAN . Statistical analysis of porosity variations in plasma sprayed Cr₃C₂- NiCr coatings. Journal of Aeronautical Materials, 2000,20(1):33-38.
[27]	ZHANG HONG-SONG, WANG FU-CHI, MA ZHUANG , et al. Quantitative analysis of pores in plasma-sprayed ZrO₂ coatings. Journal of Materials Engineering, 2006, Supplement 1: 407-425.
[28]	PRATTEN N A . The precise measurement of the density in small samples. Materials Science, 1981,16(7):1737-1747. DOI URL
[29]	ZHAO YANG, LIN LI, MA ZHI-YUAN , et al. Establishing TBC random pore model based on random media theory. China Surface Engineering, 2010,23(2):78-81.
[30]	FOX A C, CLYNE T W . Oxygen transport by gas permeation through the zirconia layer in plasma sprayed thermal barrier coating. Surface and Coatings Technology, 2004,184(2/3):311-321. DOI URL

恒温环境中ZrB₂氧化行为模拟

Simulation of ZrB₂ Oxidation Behavior at Constant Temperature Ambient

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

图/表 4

参考文献 30

相关文章 15

编辑推荐

Metrics

本文评价

[1]	穆宏赫, 王鹏飞, 施宇峰, 张中晗, 武安华, 苏良碧. 热交换坩埚下降法制备大尺寸氟化铈晶体的热场设计与优化[J]. 无机材料学报, 2023, 38(3): 288-295.
[2]	史艳磊, 孙聂枫, 徐成彦, 王书杰, 林朋, 马春雷, 徐森锋, 王维, 陈春梅, 付莉杰, 邵会民, 李晓岚, 王阳, 秦敬凯. 半密封直拉法生长6英寸磷化铟单晶热场研究[J]. 无机材料学报, 2023, 38(3): 335-342.
[3]	陈昆峰, 胡乾宇, 刘锋, 薛冬峰. 多尺度晶体材料的原位表征技术与计算模拟研究进展[J]. 无机材料学报, 2023, 38(3): 256-269.
[4]	阮景, 杨金山, 闫静怡, 游潇, 王萌萌, 胡建宝, 张翔宇, 丁玉生, 董绍明. 碳化硅纳米线增强多孔碳化硅陶瓷基复合材料的制备[J]. 无机材料学报, 2022, 37(4): 459-466.
[5]	林子扬, 常宇辰, 吴章凡, 包荣, 林文庆, 王德平. 不同模拟体液对硼硅酸盐生物活性玻璃基骨水泥矿化性能的影响[J]. 无机材料学报, 2021, 36(7): 745-752.
[6]	郑燕宁, 季军荣, 梁雪玲, 赖正杰, 陈启帆, 廖丹葵. 氮掺杂中空碳球氧化物模拟酶性能研究[J]. 无机材料学报, 2021, 36(5): 527-534.
[7]	赵林艳, 刘阳思, 席晓丽, 马立文, 聂祚仁. 基于第一性原理计算的纳米氧化钨研究进展[J]. 无机材料学报, 2021, 36(11): 1125-1136.
[8]	张志锋,王凤娟,武胜萍,蒋金洋. X-CT无损测试技术用于陶瓷涂层三维重构和孔隙率计算[J]. 无机材料学报, 2020, 35(9): 1059-1063.
[9]	赵超锋, 金佳人, 霍英忠, 孙陆, 艾玥洁. 氧化石墨烯吸附水体中酚类有机污染物的分子动力学模拟[J]. 无机材料学报, 2020, 35(3): 277-283.
[10]	李盛菘, 郑永超, 孟澍临, 吴骊珠, 钟近艺, 赵冲林. 核壳型量子点-纳米金颗粒组装体高效检测神经性毒剂模拟剂[J]. 无机材料学报, 2019, 34(8): 893-898.
[11]	李昊耕,谷红宇,章俞之,宋力昕,吴岭南,齐振一,张涛. 聚合物材料表面原子氧防护技术的研究进展[J]. 无机材料学报, 2019, 34(7): 685-693.
[12]	谢玲玲, 牛亚然, 王亮, 陈文亮, 郑学斌, 黄贞益. 等离子喷涂ZrC基涂层逐道逐层沉积残余应力模拟与实验验证[J]. 无机材料学报, 2019, 34(7): 768-774.
[13]	陈文波, 陈伦江, 刘川东, 程昌明, 童洪辉, 朱海龙. 射频热等离子体制备球形氧化铝粉末的数值模拟及实验研究[J]. 无机材料学报, 2018, 33(5): 550-556.
[14]	李国举, 范群波, 王扬卫, 史然. SiC/Al双连通复合装甲材料抗侵彻性能宏-微观跨尺度模拟[J]. 无机材料学报, 2017, 32(4): 425-430.
[15]	张磊, 马国强, 朱遂一, 杨霞, 耿直, 霍明昕. 甘氨酸辅助合成BiOI及其模拟太阳光光催化性能研究[J]. 无机材料学报, 2017, 32(2): 148-154.