白光LED用Ba2LaF7: Pr3+微晶玻璃的发光性能研究

doi:10.15541/jim20160209

无机材料学报 ›› 2016, Vol. 31 ›› Issue (10): 1046-1050.DOI: 10.15541/jim20160209

白光LED用Ba₂LaF₇: Pr³⁺微晶玻璃的发光性能研究

张志雄, 欧阳绍业, 张约品, 夏海平

(宁波大学光电子功能材料实验室, 宁波 315211)

收稿日期:2016-03-30 修回日期:2016-06-01 出版日期:2016-10-20 网络出版日期:2016-09-23
作者简介:张志雄(1990–), 男, 硕士研究生. E-mail: yangtingting990622@163.com
基金资助:
国家自然科学基金(61275180, 51472125)

Enhanced Luminescent Properties of Pr³⁺ Doped Ba₂LaF₇ Glass Ceramics for White Light-emitting Diodes

ZHANG Zhi-Xiong, OUYANG Shao-Ye, ZHANG Yue-Pin, XIA Hai-Ping

(Key Laboratory of Photo-Electronic Material, Ningbo University, Ningbo 315211, China)

Received:2016-03-30 Revised:2016-06-01 Published:2016-10-20 Online:2016-09-23
About author:ZHANG Zhi-Xiong. E-mail: yangtingting990622@163.com
Supported by:
National Natural Science Foundation of China (61275180, 51472125)

摘要/Abstract

摘要：

采用高温熔制法制备得到50SiO₂-10AlF₃-5TiO₂-30BaF₂-4LaF₃-Pr₂O₃(mol%)基质玻璃, 玻璃样品分别经640℃、660℃和690℃热处理后, 成功获得透明Ba₂LaF₇: Pr³⁺微晶玻璃且维持着较高的透明度。用XRD和TEM分析热处理前后样品的相变和结构变化, 并研究了热处理前后样品的光谱特性。结果表明: 玻璃经热处理后生成了Ba₂LaF₇微晶颗粒; 热处理前后样品光谱特性的变化表明: 热处理后掺杂的Pr³⁺离子逐渐进入到Ba₂LaF₇晶格位; 在波长443 nm的激发下, 660℃热处理过的样品实现了白光输出, 对应的三色坐标为(0.323, 0.343)。

关键词: Ba₂LaF₇: Pr³⁺, 微晶玻璃, 发光性能

Abstract:

Pr³⁺-activated 50SiO₂-10AlF₃-5TiO₂-30BaF₂-4LaF₃glass were synthesized by a conventional melting technique, and then annealed at 640℃, 660℃ and 690℃, respectively. Transparent Ba₂LaF₇: Pr³⁺ glass ceramics were successfully prepared and the transparency still remained at a high level. X-ray diffraction and transmission electron microscope were used to monitor the evolution and microstructural changes after the glass specimens were annealed at temperature increasing from 640℃ to 690℃. The spectral properties of glass and glass ceramics were also investigated. Results show that Ba₂LaF₇ nanocrystals were precipitated in the teat-treated glasses and the measured luminescent properties indicate that Pr³⁺ions are gradually incorporated into the precipitated Ba₂LaF₇ crystalline phase. Under 443 nm excitation, the Commission Internationale de L’Eclairage (CIE) chromaticity coordinates for the glass ceramics heated at 660 ℃, were estimated to be (0.323, 0.343) and exactly located in the region of white light. Current findings reveal a fact that the prepared materials have potential as replacements of commonly employed phosphors applicating in white light-emitting diodes.

Key words: Ba₂LaF₇: Pr³⁺, glass ceramics, luminescent properties

中图分类号:

TQ174

张志雄, 欧阳绍业, 张约品, 夏海平. 白光LED用Ba₂LaF₇: Pr³⁺微晶玻璃的发光性能研究[J]. 无机材料学报, 2016, 31(10): 1046-1050.

ZHANG Zhi-Xiong, OUYANG Shao-Ye, ZHANG Yue-Pin, XIA Hai-Ping. Enhanced Luminescent Properties of Pr³⁺ Doped Ba₂LaF₇ Glass Ceramics for White Light-emitting Diodes[J]. Journal of Inorganic Materials, 2016, 31(10): 1046-1050.

图/表 7

图1 组分为50SiO2-10AlF3-5TiO2-30BaF2-4LaF3-Pr2O3(mol%)的样品DSC曲线

Fig. 1 DSC curve of as-prepared 50SiO2-10AlF3-5TiO2-30BaF2- 4LaF3-Pr2O3(mol%)

图2 玻璃和微晶玻璃样品的XRD图谱以及Ba2LaF7相标准卡片

Fig. 2 XRD patterns of samples PG, GC640, GC660, GC690 and the standard line graphs of Ba2LaF7 crystal (48-0099)

图3 玻璃以及微晶玻璃样品的透射光谱

Fig. 3 Transmission spectra of samples PG, GC640, GC660 and GC690

图4 样品的TEM照片以及SAED图像

Fig. 4 TEM image of GC660 and the corresponding SAED patterns

图5 玻璃及微晶玻璃样品的激发光谱

Fig. 5 Excitation spectra of samples PG, GC640, GC660 and GC690

图6 玻璃及微晶玻璃样品的发射光谱

Fig. 6 Emission spectra of PG, GC640, GC660 and GC690

图7 样品PG、GC660色度图(坐标点分别对应1, 2)

Fig.7 Chromaticity coordinates of samples PG, GC660 under 443 nm excitation (point 1, 2, respectively)

参考文献 12

[1]	BERGH A, CRAFORD G, DUGGAL A, et al.The Promise and challenge of solid-state lighting. Phys. Today, 2001, 54(12): 42-47.
[2]	SATO Y, TAKAHASHI N, SATO S.Full-color fluorescent display devices using near-UV light-emitting diode. Jpn. Appl. Phys.,Part 2, 1996, 35(7A): L838-L839.
[3]	HUH Y D, SHIM J H, KIM Y, et al.Optical properties of three-band white light-emitting diodes.J. Electronchem. Soc., 2003, 150(2): H57-H60.
[4]	LUO Q, FAN X, QIAO X, et al.Eu2+-doped glass ceramics containing BaF2 nanocrystals as a potential blue phosphor for UV-LED. J. Am. Ceram. Soc., 2009, 92(4): 942-944.
[5]	ZHANG W H, ZHANG Y P, OUYANG S Y Z, et al. Luminescent properties of Eu2+-doped BaGdF5 glass ceramics a potential blue phosphor for ultra-violet light-emitting diode. J. Appl. Phys., 2015, 117(2): 023113-1-6.
[6]	ZHANG W H, OUYANG S Y, ZHANG Z X, et al.Luminescent properties of Eu3+-doped glass ceramics containing BaGdF5 nanocrystals under NUV-excitation for W-LEDs. Ceram. Int., 2015, 41(10): 14035-14040.
[7]	ZHANG W H, ZHANG Y P, OUYANG S Y, et al. Enhanced luminescent properties of Sm3+ doped glass ceramics- as potential red-orange phosphor for white light-emitting diodes. Mater. Lett., 2015(160): 459-462.
[8]	OUYANG S Y, ZHANG W H, ZHANG Z X, et al. Near-white light-emitting Dy3+-doped transparent glass ceramics containing Ba2LaF7 nanocrystals. Chin. Opt. Lett., 2015, 13(9): 091601-1-4.
[9]	YANG B, WANG Q, ZHANG W H, et al. Luminescent properties of Tb3+-doped transparent glass ceramics. J. Lumin., 2015(158): 390-395.
[10]	WANG Q, OUYANG S Y, ZHANG W H, et al.Luminescent properties of Ce3+-doped transparent oxyfluoride glass ceramics containing BaGdF5 nanocrystals.J. Rare Earth, 2015, 8987(1): 13-19.
[11]	WANG Q, ZHANG W H, OUYANG S Y, et al.Luminescent properties of Ce3+ ion and Tb3+ ion co-doped transparent oxyfluoride glass ceramics containing BaGdF5 nanocrystals.J. Non-Cryst. Solids, 2015, 411(1): 35-39.
[12]	MAHLIK S, GRINBERG M, KAMINSKII A A, et al.Luminescence of Ca(NbO3)2: Pr3+ at ambient and high hydrostatic pressure.J. Lumin., 2009, 129(10): 1219-1224.

[1]	王志强, 吴济安, 陈昆峰, 薛冬峰. 大尺寸Er,Yb:YAG单晶的生长及其性能[J]. 无机材料学报, 2023, 38(3): 329-334.
[2]	杨金萍, 季文玲, 张浩, 刘盼, 崔燚, 魏恒勇. Eu ³⁺掺杂的多孔锆酸镧粉体制备及发光性能研究[J]. 无机材料学报, 2019, 34(7): 727-733.
[3]	焦志伟, 段翠翠, 周伟, 刘峰斌, 杨越, 赵攀, 项俊帆. Ni²⁺掺杂尖晶石相透明微晶玻璃制备及光学性能[J]. 无机材料学报, 2018, 33(6): 673-677.
[4]	屈婧婧, 魏星, 刘飞, 袁昌来, 陈国华, 黄先培. 热处理对Mg-Al-Si-Ti-B系微晶玻璃析晶及介电性能的影响[J]. 无机材料学报, 2018, 33(12): 1309-1315.
[5]	张庆福, 李臣, 宋志国, 李永进, 邱建备, 杨正文. F/Cl比对卤磷酸钙固溶体Bi离子掺杂位点及价态的调控[J]. 无机材料学报, 2017, 32(6): 661-666.
[6]	龚伟, 李华, 周黎明, 白朝中, 王恩泽. 3Y-TZP/LZAS微晶玻璃功能梯度涂层的微观结构与性能[J]. 无机材料学报, 2017, 32(1): 63-68.
[7]	吴霜, 刘波, 陈士伟, 张娟楠, 刘小林, 顾牡, 黄世明, 倪晨, 薛超凡. Lu₂SiO₅: Ce³⁺透明薄膜制备及其发光性能研究[J]. 无机材料学报, 2016, 31(9): 948-954.
[8]	毛启楠, 李鹤, 季振国, 席俊华, 张峻, 孔哲. Eu²⁺和Dy³⁺掺杂浓度对Sr₂MgSi₂O₇材料的荧光和长余辉性能的影响[J]. 无机材料学报, 2016, 31(8): 819-826.
[9]	吴霜, 刘波, 邱志澈, 陈士伟, 张娟楠, 刘小林, 顾牡, 黄世明, 倪晨. LuTaO₄:Ln³⁺(Ln=Eu,Tb)透明薄膜制备改进与其发光性能研究[J]. 无机材料学报, 2016, 31(4): 372-376.
[10]	殷海荣, 刘晶, 乔荫颇, 李艳肖, 张攀, 周沁, 杨晨. 锶含量对稀土Eu掺杂锶钙羟基磷灰石发光性能及取代位置的影响[J]. 无机材料学报, 2016, 31(10): 1103-1109.
[11]	李要辉, 王晋珍, 黄幼榕. 硅碱钙石微晶玻璃的析晶特性及其增韧机理研究[J]. 无机材料学报, 2015, 30(9): 977-983.
[12]	张书娴, 崔博, 王宏志, 李耀刚, 张青红. 柔性Eu³⁺掺杂SiO₂纳米纤维薄膜的制备及其发光性能[J]. 无机材料学报, 2015, 30(7): 719-724.
[13]	彭霞, 李淑星, 刘学建,黄毅华, 黄政仁, 李会利. Eu²⁺/Tb³⁺掺杂的Sr₂Si₅N₈基荧光粉的制备与发光性能[J]. 无机材料学报, 2015, 30(4): 397-400.
[14]	李金生, 孙旭东, 李晓东, 刘绍宏, 朱琦. 硬脂酸盐熔融法合成(Y,Lu)AG:Ce荧光粉及荧光性能研究[J]. 无机材料学报, 2015, 30(2): 177-182.
[15]	朱巍巍, 陈继春. 微晶玻璃焊料在连接过程中的晶化行为研究[J]. 无机材料学报, 2015, 30(12): 1310-1314.

白光LED用Ba₂LaF₇: Pr³⁺微晶玻璃的发光性能研究

Enhanced Luminescent Properties of Pr³⁺ Doped Ba₂LaF₇ Glass Ceramics for White Light-emitting Diodes

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

图/表 7

参考文献 12

相关文章 15

编辑推荐

Metrics

本文评价