Ba8Ga15XSi30(X= Ga、Zn、Cu)的热电性能研究

doi:10.15541/jim20140403

摘要/Abstract

摘要：

采用电弧炉熔炼、球磨、放电等离子烧结的方法合成了系列第I类笼状化合物Ba₈Ga₁₅XSi₃₀(X=Ga、Zn、Cu)。研究了Zn、Cu对Ga的替代对材料结构以及热电性能的影响。结果表明, 相比于Ba₈Ga₁₆Si₃₀, Zn、Cu的掺杂使得样品的晶格常数减小, 热导率降低, Seebeck系数的绝对值增大, ZT值有明显的升高。

关键词: I类笼状化合物, 晶格常数, 热电性能

Abstract:

A series of Ba₈Ga₁₅XSi₃₀ (X=Ga、Zn、Cu) clathrate samples were prepared by combining arc melting, ball milling and spark plasma sintering (SPS) techniques. The crystal structure and thermoelectric properties of all samples were studied. Compared with Ba₈Ga₁₆Si₃₀, the lattice constant a decreases as one Ga is replaced by Zn or Cu. What’s more, thermal conductivity decreases and magnitude of Seebeck coefficient increases with Zn or Cu doping. Consequently, thermoelectric figure of merit ZT increases significantly.

Key words: type-I clathrate, lattice constant, thermoelectric properties

中图分类号:

O469

刘丽华, 宋奔升, 栗峰, 王镇, 潘浩瀚, 李阳. Ba₈Ga₁₅XSi₃₀(X= Ga、Zn、Cu)的热电性能研究[J]. 无机材料学报, 2015, 30(3): 261-266.

LIU Li-Hua, SONG Ben-Sheng, LI Feng, WANG Zhen, PAN Hao-Han, LI Yang. Thermoelectric Properties of Ba₈Ga₁₅XSi₃₀ (X= Ga, Zn, Cu)[J]. Journal of Inorganic Materials, 2015, 30(3): 261-266.

图/表 7

图1 名义配比为Ba8Ga15XSi30(X=Ga、Zn、Cu)样品的XRD精修图谱

Fig. 1 XRD refinement for samples with nominal formula Ba8Ga15XSi30(X=Ga、Zn、Cu)

表1 Ba8Ga15XSi30 (X=Ga、Zn、Cu) 样品EDS及GSAS成分分析结果

Table 1 Analytical results of chemical components for Ba8Ga15XSi30 (X=Ga、Zn、Cu) by EDS and GSAS

Nominal composition	Actual composition by GSAS	Actual composition by EDS
Ba₈Ga₁₆Si₃₀	Ba_8.00Ga_14.4(9)Si_31.5(1)	Ba_8.0(2)Ga_14.8(6)Si_31.1(4)
Ba₈Ga₁₅ZnSi₃₀	Ba_8.00Ga_14.4(0)Zn_1.0(5)Si_30.5(5)	Ba_7.9(7)Ga_14.5(7)Zn_1.0(0)Si_30.4(3)
Ba₈Ga₁₅CuSi₃₀	Ba_8.00Ga_14.4(5)Cu_0.8(5)Si_30.7(0)	Ba_8.0(0)Ga_14.7(6)Cu_0.7(9)Si_30.4(5)

图2 Ba8Ga15XSi30(X=Ga、Zn、Cu)的Seebeck系数S随温度的变化曲线

Fig. 2 Temperature dependence of the Seebeck coefficient S for Ba8Ga15XSi30 (X=Ga、Zn、Cu)

图3 Ba8Ga15XSi30(X=Ga、Zn、Cu)的电导率σ随温度的变化曲线

Fig. 3 Temperature dependence of the electrical conductivity σ of Ba8Ga15XSi30 (X=Ga、Zn、Cu)

图4 Ba8Ga15XSi30(X=Ga、Zn、Cu)的热导率κ 随温度的变化曲线

Fig. 4 Thermal conductivity κ versus temperature of Ba8Ga15XSi30 (X=Ga、Zn、Cu)

图5 Ba8Ga15XSi30(X=Ga、Zn、Cu)的晶格热导率κL随温度的变化曲线

Fig. 5 Lattice thermal conductivity κL versus temperature of Ba8Ga15XSi30 (X=Ga、Zn、Cu)

图6 Ba8Ga15XSi30(X=Ga、Zn、Cu)的ZT值随温度的变化曲线

Fig. 6 Thermoelectric figure of merit ZT of Ba8Ga15XSi30 (X=Ga、Zn、Cu)

参考文献 32

[1]	ROSS J H, LI Y.Nanoscale Magnetic Materials and Applications. New York: Springer-Verlag, 2009, 105-122.
[2]	VENKATASUBRAMANIAN R, SIIVOLA E, COLPITTS T, et al.Thin-film thermoelectric devices with high room-temperature figures of merit.Nature, 2001, 413(6856): 597-602.
[3]	COHN J L, NOLAS G S, FESSATIDIS V, et al.Glasslike heat conduction in high-mobility crystalline semiconductors.Phys. Rev. Lett., 1999, 82(4): 779-782.
[4]	TOBERER E S, MAY A F, SNYDER G J.Zintl chemistry for designing high efficiency thermoelectric materials.Chem. Mater., 2010, 22(3): 624-634.
[5]	刘恩科, 朱秉升, 罗晋生. 半导体物理学, 7版. 北京: 电子工业出版社, 2011: 350-364.
[6]	SHI X, XI L L, YANG J, et al.Basic physics in thermoelectrics.Physics, 2011, 40(11): 710-718.
[7]	SOOTSMAN J R, CHUNG D Y, KANATZIDIS M G.New and old concepts in thermoelectric materials.Angew. Chem. Int. Ed., 2009, 48(46): 8616-8639.
[8]	TOBERER E S, CHRISTENSEN M, IVERSEN B B, et al. High temperature thermoelectric efficiency in Ba8Ga16Ge30. Phys. Rev. B, 2008, 77(7): 075203-1-8.
[9]	YAN X, CHEN M X, LAUMANN S, et al. Thermoelectric properties of Ba-Cu-Si clathrates. Phys. Rev. B, 2012, 85(16): 165127-1-10.
[10]	BLAKE N P,MøLLNITZ L , KRESSE G,et al.. Why clathrates are good thermoelectric: a theoretical study of Sr8Ga16Ge30. J. Chem. Phys., 1999, 111(7): 3133-3144.
[11]	SHEVELKOV A V, KOVNIR K. Zintl Clathrates.Berlin: Springer-Verlag Berlin Heidelberg, 2011: 97-142.
[12]	KUZNETSOV V L, KUZNETSOVA L A, KALIAZIN A E, et al.Preparation and thermoelectric properties of A8IIB16IIIB30IV clathrate compounds.J. Appl. Phys., 2000, 87(11): 7871-7875.
[13]	ZHANG Y G, LEE P L, NOLAS G S, et al.Gallium distribution in the clathrates Sr8Ga16Ge30 and Sr4Eu4Ga16Ge30 by resonant diffraction.Appl. Phys. Lett. , 2002, 80(16): 2931-2933.
[14]	TRITT T M, SUBRAMANIAN M A.Thermoelectric materials, phenomena, and applications: a bird's eye view.MRS Bulletin, 2006, 31(3): 188-198.
[15]	ANNO H, HOKAZONO M, SHIRATAKI R, et al.Crystallographic, thermoelectric, and mechanical properties of polycrystalline type-I Ba8Al16Si30-based clathrates.J. Mater. Sci., 2013, 48(7): 2846-2854.
[16]	ANNO H, YAMADA H, NAKABAYASHI T, et al.Gallium composition dependence of crystallographic and thermoelectric properties in polystalline type-I Ba8GaxSi46-x (nominal x=14-18) clathrates prepared by combining arc melting and spark plasma sintering methods.J. Solid State Chem., 2012, 193: 94-104.
[17]	ANNO H, YAMADA H, NAKABAYASHI T, et al. Influence of preparation conditions on thermoelectric properties of Ba8Ga16Si30 clathrate by combining arc melting and spark plasma sintering methods. Journal of Physics: Conference Series, 2012, 379(1): 012007-1-7.
[18]	BLAKE N P, BRYAN D, LATTURNER S, et al.Structure and stability of clathrates Ba8Ga16Ge30, Sr8Ga16Ge30, Ba8Ga16Si30, and Ba8In16Sn30.J. Chem. Phys., 2001, 114(22): 10063-10074.
[19]	DENG S K, TANG X F, TANG R S.Synthesis and high temperature thermoelectric transport properties of Si-based type-I clathrates.Chin. Phys. B, 2009, 18(7): 3084-3089.
[20]	SALES B C, CHAKOUMAKOS B C, JIN R, et al. Structural, magnetic, thermal,transport properties of X8Ga16Ge30 (X=Eu, Sr, Ba) single crystals. Phys. Rev. B, 2001, 63(23): 245113-1-8.
[21]	CEDERKRANTZ D, SARAMAT A, SNYDER G J, et al. Thermal stability and thermoelectric properties of p-type Ba8Ga16Ge30 clathrates. J. Appl. Phys., 2009,106(7): 074509-1-7.
[22]	SHI X, YANG J, BAI S, et al.On the design of high-efficiency thermoelectric clathrates through a systematic cross-substitution of framework elements.Adv. Funct. Mater., 2010, 20(5): 755-763.
[23]	FALMBIGL M, GRYTSIV A, ROGL P, et al.Tuning of band gap and thermoelectric properties of type-I clathrate Ba8NixZnyGe46-x-y-zSnz.J. Alloy. Compd., 2013, 567: 65-72.
[24]	JOHNSEN S, BENTIEN A, MADSEN G H, et al. Crystal structure and transport properties of nickel containing germanium clathrates , Phys. Rev. B , 2007, 76(24): 245126-1-9.
[25]	JOHNSEN S, BENTIEN A, MADSEN G H, et al.Crystal structure, band structure, and physical properties of Ba8Cu6-xGe40+x (0≤x ≤0.7).Chem. Mater., 2006, 18(19): 4633-4642.
[26]	HOKAZONO M, ANNO H, MATSUBARA K.Effect of Cu substitution on thermoelectric properties of Ge clathrates.Mater. Trans., 2005, 46(7): 1485-1489.
[27]	BEDNAR I, ROYANIAN E, BÜHLER-PASCHEN S, et al. Giant thermopower at low temperatures in novel clathrates Ba8{Cu, Zn}xGe46-x.J. Electron. Mater., 2010, 39(9): 1687-1691.
[28]	DENG S K, TANG X F, LI P, et al. High temperature thermoelectric transport properties of p-type Ba8Ga16AlxGe30-x type-I clathrates with high performance. J. Appl. Phys., 2008, 103(7): 073504-1-6.
[29]	DENG S K, TANG X F, ZHANG Q J.Synthesis and thermoelectric properties of p-type Ba8Ga16ZnxGe30-x type-I clathrates, J. Appl.Phys., 2007, 102(4): 043702-1-5.
[30]	LARSON A C, VON DREELE R B V. General Structure Analysis System (GSAS). New Mexico: Los Alamos National Laboratory, 2004: 86-748.
[31]	YANG L, WANG Y, LIU T, et al.Cooper position in type-I Ba8Cu4Si42 clathrate.J. Solid State Chem., 2005, 178(6): 1773-1777.
[32]	DENG S K, TANG X F, XIONG C, et al.Synthesis and electrical transmission characteristics of type-I Ba8Ga16ZnxSi30-x.Chinese Journal of Semiconductors, 2007, 28(4): 553-557.

Ba₈Ga₁₅XSi₃₀(X= Ga、Zn、Cu)的热电性能研究

Thermoelectric Properties of Ba₈Ga₁₅XSi₃₀ (X= Ga, Zn, Cu)

RichHTML

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

图/表 7

参考文献 32

相关文章 15

编辑推荐

Metrics

本文评价

[1]	汪波, 余健, 李存成, 聂晓蕾, 朱婉婷, 魏平, 赵文俞, 张清杰. Gd/Bi_0.5Sb_1.5Te₃热电磁梯度复合材料的服役稳定性[J]. 无机材料学报, 2023, 38(6): 663-670.
[2]	贺丹琪, 魏明旭, 刘蕤之, 汤志鑫, 翟鹏程, 赵文俞. 一步法制备重费米子YbAl₃热电材料及其性能提升[J]. 无机材料学报, 2023, 38(5): 577-582.
[3]	林思琪, 李艾燃, 付晨光, 李荣斌, 金敏. Zintl相Mg₃X₂(X=Sb, Bi)基晶体生长及热电性能研究进展[J]. 无机材料学报, 2023, 38(3): 270-279.
[4]	程成, 李建波, 田震, 王鹏将, 康慧君, 王同敏. In₂O₃/InNbO₄复合材料的热电性能研究[J]. 无机材料学报, 2022, 37(7): 724-730.
[5]	刘丹, 赵亚欣, 郭锐, 刘艳涛, 张志东, 张增星, 薛晨阳. 退火条件对磁控溅射MgO-Ag₃Sb-Sb₂O₄柔性薄膜热电性能的影响[J]. 无机材料学报, 2022, 37(12): 1302-1310.
[6]	任培安, 汪聪, 訾鹏, 陶奇睿, 苏贤礼, 唐新峰. Te与In共掺杂对Cu₂SnSe₃热电性能的影响[J]. 无机材料学报, 2022, 37(10): 1079-1086.
[7]	逯旭, 侯绩翀, 张强, 樊建锋, 陈少平, 王晓敏. Mg含量对Mg₃₍₁₊_z₎Sb₂化合物热电传输性能的影响[J]. 无机材料学报, 2021, 36(8): 835-840.
[8]	杨枭, 苏贤礼, 鄢永高, 唐新峰. (GeTe)_nBi₂Te₃的结构与热电性能研究[J]. 无机材料学报, 2021, 36(1): 75-80.
[9]	李周, 肖翀. 异层等价离子双掺杂策略优化BiCuSeO的热电性能[J]. 无机材料学报, 2019, 34(3): 294-300.
[10]	胡慧珊, 杨君友, 辛集武, 李思慧, 姜庆辉. SnO的歧化反应对SnTe热电性能的优化[J]. 无机材料学报, 2019, 34(3): 315-320.
[11]	黄志成, 姚瑶, 裴俊, 董金峰, 张波萍, 李敬锋, 尚鹏鹏. n型SnS热电材料的制备与性能研究[J]. 无机材料学报, 2019, 34(3): 321-327.
[12]	檀小芳, 端思晨, 王泓翔, 吴庆松, 李苗苗, 刘国强, 徐静涛, 谈小建, 邵和助, 蒋俊. 多掺杂协同调控碲化锡热导率和功率因子提升热电性能[J]. 无机材料学报, 2019, 34(3): 335-340.
[13]	刘虹霞, 李文, 张馨月, 李娟, 裴艳中. (Ag₂Se)_1-_x(Bi₂Se₃)_x的热电性能研究[J]. 无机材料学报, 2019, 34(3): 341-348.
[14]	李松浩, 张忻, 刘洪亮, 郑亮, 张久兴. Ag掺杂SnSe化合物的制备及热电性能[J]. 无机材料学报, 2016, 31(7): 751-755.
[15]	姚铮, 仇鹏飞, 李小亚, 陈立东. n型填充方钴矿热电材料的快速制备研究[J]. 无机材料学报, 2016, 31(12): 1375-1382.