粉末粒径对热压烧结碳化硼致密化及力学性能的影响

doi:10.3724/SP.J.1077.2013.13004

无机材料学报 ›› 2013, Vol. 28 ›› Issue (10): 1062-1066.DOI: 10.3724/SP.J.1077.2013.13004

粉末粒径对热压烧结碳化硼致密化及力学性能的影响

杜贤武, 张志晓, 王为民, 傅正义, 王皓

(武汉理工大学材料复合新技术国家重点实验室, 武汉 430070)

收稿日期:2013-01-04 修回日期:2013-03-09 出版日期:2013-10-20 网络出版日期:2013-09-18
作者简介:杜贤武(1989-), 男, 博士研究生. E-mail: duxianwu_nihao@163.com
基金资助:
中日韩A3前瞻计划(50821140308)

Effect of Particle Size on Densification and Mechanical Properties of Hot-pressed Boron Carbide

DU Xian-Wu, ZHANG Zhi-Xiao, WANG Wei-Min, FU Zheng-Yi, WANG Hao

(Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070, China)

Received:2013-01-04 Revised:2013-03-09 Published:2013-10-20 Online:2013-09-18
About author:DU Xian-Wu. E-mail: duxianwu_nihao@163.com
Supported by:
Asia 3 Foresight Program (50821140308)

摘要/Abstract

摘要： 采用平均粒径分别为3.5 μm、1.5 μm和200 nm的碳化硼粉体为原料经1850℃热压烧结制备了碳化硼陶瓷, 研究了粉体粒径对陶瓷烧结致密化过程及其性能的影响。根据保温时间对线收缩率的影响及热压初期的塑性流动机理, 得出了不同粉体间烧结初期的激活能差。结果表明: 在相同工艺条件下, 随着粉体平均粒径的减小, 粉体的扩散激活能降低, 致密化初始温度降低, 而且完成塑性流动所需时间也会明显缩短, 致密化速率加快, 致密度增大; 碳化硼陶瓷的显微结构与力学性能亦随着粉体粒径的减小而改善; 1850℃保温1 h后, 平均粒径为200 nm的粉体制备的碳化硼陶瓷相对密度可达90.5%, 硬度为(17±1.8) GPa。

关键词: 碳化硼, 致密化, 热压, 力学性能

Abstract: Monolithic B₄C ceramics were prepared by hot-pressing using three types of B4C powders with average particle of 3.5 μm, 1.5 μm and 200 nm, respectively. The effect of particle size on densification and microstructure of sintered ceramics was studied. The activation energy difference of the starting powders in the initial sintering stage was obtained in terms of dwelling time as a function of linear shrinkage and plastic deformation mechanism. The result shows that at the same process, the diffusion activation energy and densification initial temperature of the powders decrease with the mean particle size decreasing, and the time of plastic flow in the initial sintering stage is also shortened markedly, while the relative density and densification rate are higher. The microstructure and mechanical properties of sinterd samples are also improved with mean particle size decreasing. The relative density of 90.5% and hardness of (17±1.8) GPa are achieved for the B4C ceramics sintered from the powders with mean particle size of 200 nm for 1 h at 1850℃.

Key words: boron carbide, densification, hot pressing, mechanical property

中图分类号:

TQ174

杜贤武, 张志晓, 王为民, 傅正义, 王皓. 粉末粒径对热压烧结碳化硼致密化及力学性能的影响[J]. 无机材料学报, 2013, 28(10): 1062-1066.

DU Xian-Wu, ZHANG Zhi-Xiao, WANG Wei-Min, FU Zheng-Yi, WANG Hao. Effect of Particle Size on Densification and Mechanical Properties of Hot-pressed Boron Carbide[J]. Journal of Inorganic Materials, 2013, 28(10): 1062-1066.

参考文献

[1] Thevent F. Boron carbide-a comprehensive review. J. Eur. Ceram. Soc., 1990, 6: 205-225.

[2] Suri K A, Subramanian C, Sonber J K. Synthesis and consolidation of boron carbide: a review. International Materials Reviews., 2010, 55(1): 4-40.

[3] Hayun S, Weizmann A, Dariel M P, et al. The effect of particle size distribution on the microstructure and the mechanical properties of boron carbide based reaction bonded composites. Int. J. Appl. Ceram. Technol., 2009, 6(4): 492-500.

[4] Yamada S, Hirao K, Yamauchi Y. Densification behaviour and mechanical properties of pressure-less-sintered B4C-CrB2 ceramics. J. Mater. Sci., 2002, 37: 5007-5012.

[5] PENG Ke-wu, WU Wen-yuan, XU Jing-yu, et al. Study on mechanical proper ties and fracture mechanism of B4C/Al composite. Hot Working Technology, 2007, 36(4): 1-4.

[6] DING Shuo, WEN Guang-Wu, LEI Ting-Quan, et al. Microstructure and properties of polycarbosilane transferred nano SiC reinforced B4C matrix composites. Journal of Inorganic Materials, 2002, 17(5): 1013-1018.

[7] MA Qian-Cheng, ZHANG Guo-Jun, KAN Yan-Mei, et al. Densification and mechanical properties of boron carbide ceramics with addition of silicon hexaboride. Journal of Inorganic Materials, 2008, 23(6): 1175-1178.

[8] Xu Changming, Flodstrom Katarina, Esmaeilzadeh Saeid. Low temperature densification of B4C ceramics with CaF2/Y2O3 addtives. Int. Journal of Refractory Metals and Hard Materials., 2012, 35: 311-314.

[9] Ye Feng, Zhou Zhaoping, Zhang Haijiao, et al. Densification and mechanical properties of spark plasma sintered B4C with Si as a sintering aid. J. Am. Ceram. Soc., 2010, 93(10): 2956-2959.

[10] Yue XinYan, Zhao ShuMao, Lv Peng, et al. Synthesis and properties of hot pressed B4C-TiB2 ceramic composite. Materials Science and Engineering A., 2010, 527: 7215-7219.

[11] Coble R L. Diffusion models for hot pressing with suvfaee energy and pressure effects as driving forces. J. Appl. Phys., 1970, 41(12): 4798-4807.

[12] 高端平, 李晓光, 施剑林, 等. 先进陶瓷物理与化学原料及技术. 北京: 科学出版社, 2000: 358-362.

[13] Murray P, Livey D T, Williams J, et al.Ceramic Fabrication Process. New York, 1958.

[14] Shi Jianlin, Lin Zuxiang, Yang Zhizhou. Hot pressed Na-beta-alumina: densification mechanism of hot pressed Na-beta-Al2O3. Journal of The Chinese Ceramic Society,-1987, 15(3): 241-247

[15] Bouvard D, Meister T. Modelling bulk viscosity of powder aggregate during sintering. Modelling Simul. Mater. Sci. Eng., 2000, 8(3): 377-388.

[16] 贺新福, 郭聪慧, 尹邦跃. 超细钨粉热压烧结致密化过程的计算机模拟. 2006年全国核材料学术交流会论文集. 北京, 2006: 79-83.

粉末粒径对热压烧结碳化硼致密化及力学性能的影响

Effect of Particle Size on Densification and Mechanical Properties of Hot-pressed Boron Carbide

RichHTML

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	安文然, 黄晶琪, 卢祥荣, 蒋佳宁, 邓龙辉, 曹学强. 热处理温度对LaMgAl₁₁O₁₉涂层热/力学性能的影响[J]. 无机材料学报, 2022, 37(9): 925-932.
[2]	张叶, 曾宇平. 自蔓延高温合成氮化硅多孔陶瓷的研究进展[J]. 无机材料学报, 2022, 37(8): 853-864.
[3]	夏乾, 孙是昊, 赵义亮, 张翠萍, 茹红强, 王伟, 岳新艳. 碳化硼颗粒级配对硅反应结合碳化硼复合材料结构与性能的影响[J]. 无机材料学报, 2022, 37(6): 636-642.
[4]	洪督, 牛亚然, 李红, 钟鑫, 郑学斌. 等离子喷涂TiC-Graphite复合涂层摩擦磨损性能[J]. 无机材料学报, 2022, 37(6): 643-650.
[5]	徐谱昊, 张相召, 刘桂武, 张明芬, 桂新易, 乔冠军. Al-Ti合金钎焊SiC陶瓷接头界面微观结构与力学性能[J]. 无机材料学报, 2022, 37(6): 683-690.
[6]	丁健翔, 张凯歌, 柳东明, 郑伟, 张培根, 孙正明. Ti₃AlC₂陶瓷及其衍生物Ti₃C₂T_x增强的Ag基电接触材料[J]. 无机材料学报, 2022, 37(5): 567-573.
[7]	杨勇, 郭啸天, 唐杰, 常浩天, 黄政仁, 胡秀兰. 非氧化物陶瓷光固化增材制造研究进展及展望[J]. 无机材料学报, 2022, 37(3): 267-277.
[8]	蔚海浪, 曹学强, 邓龙辉, 蒋佳宁. LaMeAl₁₁O₁₉/YSZ热障涂层热力学性能和热循环寿命[J]. 无机材料学报, 2022, 37(12): 1259-1266.
[9]	孙扬善, 杨治华, 蔡德龙, 张正义, 柳琪, 房树清, 冯良, 石丽芬, 王友乐, 贾德昌. 粉末烧结法制备α-堇青石基玻璃陶瓷的析晶动力学和性能[J]. 无机材料学报, 2022, 37(12): 1351-1357.
[10]	吴西士, 朱云洲, 黄庆, 黄政仁. 树脂基多孔碳孔结构对C_f/SiC复合材料连接性能的影响[J]. 无机材料学报, 2022, 37(12): 1275-1280.
[11]	孙鲁超, 周翠, 杜铁锋, 吴贞, 雷一明, 李家麟, 苏海军, 王京阳. 光悬浮区熔定向凝固Al₂O₃/Er₃Al₅O₁₂和Al₂O₃/Yb₃Al₅O₁₂共晶陶瓷的制备与性能研究[J]. 无机材料学报, 2021, 36(6): 652-658.
[12]	梁汉琴, 尹金伟, 左开慧, 夏咏锋, 姚冬旭, 曾宇平. 添加BaTiO₃的热压烧结Si₃N₄陶瓷的力学和介电性能[J]. 无机材料学报, 2021, 36(5): 535-540.
[13]	王皓轩, 刘巧沐, 王一光. 高熵过渡金属碳化物陶瓷的研究进展[J]. 无机材料学报, 2021, 36(4): 355-364.
[14]	吕莎莎, 祖宇飞, 陈国清, 赵伯俊, 付雪松, 周文龙. 陶瓷颗粒增强Cr_0.5MoNbWTi难熔高熵合金复合材料的制备及其力学性能[J]. 无机材料学报, 2021, 36(4): 386-392.
[15]	金敏, 白旭东, 赵素, 张如林, 陈玉奇, 周丽娜. 坩埚下降法生长SnSe单晶及其力学性能研究[J]. 无机材料学报, 2021, 36(3): 313-318.