低氟TFA-MOD工艺快速制备YBCO超导厚膜的研究

汤 潇, 索红莉, 叶 帅, 刘 敏, 吴紫平, 周美玲   

  1. (北京工业大学 材料学院, 新型功能材料教育部重点实验室, 北京 100022)
  • 收稿日期:2009-11-10 修回日期:2010-03-29 出版日期:2010-09-20 网络出版日期:2010-08-25
  • 基金资助:

    国家973计划(2006CB601005); 北京市自然科学基金(2072004); 教育部高等学校全国优秀博士学位论文作者专项基金(200331); 北京工业大学111人才工程基金

Rapid Synthesis of YBCO Thick Superconducting Films by Low Fluorine TFA-MOD Method

TANG Xiao, SUO Hong-Li, YE Shuai, LIU Min, Wu Zi-Ping, ZHOU Mei-Ling   

  1. (Key Laboratory of Advanced Functional Materials, Ministry of Education, College of Materials Science and Engineering, Beijing University of Technology, Beijing 100022, China)
  • Received:2009-11-10 Revised:2010-03-29 Published:2010-09-20 Online:2010-08-25

PDF (PC)

1885

被引次数

15 | 1

摘要：

为提高TFA-MOD工艺制备YBCO薄膜的生产效率, 实验采用了丙烯酸盐对传统三氟乙酸盐进行部分替换. 由于前驱溶液中氟含量的减少, 低温预处理过程升温速率可达到300℃/h; 并通过对低温预烧工艺中气氛的调整, 避免了增稠剂二乙醇胺的添加对薄膜质量造成的不利影响, 使其添加上限达到0.75g/5mL. 经过工艺改进, 单次涂膜厚度可达到1μm. 虽然由于厚度的增加, 表面有a轴晶粒出现, 但薄膜内部仍具有较优的微观结构. 其临界电流密度(Jc)及临界转变温度(Tc)分别达到3.5MA/cm2和90K.

关键词: YBCO, TFA-MOD, 丙烯酸, 二乙醇胺

Abstract:

To elevate the productivity of high critical current YBCO superconducting films by TFA-MOD processing, traditional trifluoroacetate (TFA) was replaced by acrylic acetate partially. Since the fluorine content in precursor solution was decreased, the ramping rate in decomposition process reached 300℃/h. Meanwhile the atmosphere was also adjusted to avoid the fatal effect of diethanolamine (DEA), and to increase thickness of YBCO film. By increasing the maximum of DEA addition to 0.75g/5mL, the thickness of film reaches 1μm. While some a-axis grains dispersed on the film surface are probably ascribed to the rise of thickness, the YBCO film has good interior microstructures overall. As a result, the highest critical current density is 3.5MA/cm2 and the critical temperature is 90K as well.

Key words: YBCO, TFA-MOD, acrylic acid, diethanolamine