Ni/（TiO2+Urea）纳米核壳颗粒电流变行为

doi:10.3724/SP.J.1077.2010.00259

摘要/Abstract

摘要： 通过Sol-Gel法制备出Ni颗粒表面均匀包覆尿素掺杂二氧化钛涂层的纳米核壳颗粒Ni/（TiO^₂+Urea）,对其电流变行为进行了研究. 结果表明颗粒热处理温度和尿素加入量对其电流变活性有较大影响,热处理温度高于320℃以后剪切强度明显降低;尿素与Ti的质量比为30%时,剪切强度达到40kPa（4kV/mm直流电场),是无尿素时的10倍,但过量的尿素使强度下降. 显微镜观察直流电场下电流变液的结构显示,尿素与Ti的质量比为30%时核壳颗粒电流变液形成的柱粗壮、致密,尿素过量时柱产生断裂,无尿素时柱纤细、疏松. 尿素中的极性分子是影响Ni/（TiO₂+Urea）颗粒电流变行为的重要因素.

关键词: 电流变效应, 纳米镍, 极性分子, 二氧化钛

Abstract: The Ni/（TiO₂+Urea）coreshell nano particles composed of nano Ni particles and ureadoped TiO₂ coating, were synthesized by using SolGel method, and their electrorheological (ER) behaviors were investigated. The results show that ER activity of the particles are closely associated with heattreatment temperature and urea content. The shear stress decreases when the particles is heattreated above 320℃. When the mass ratio of urea to Ti is 30%, the shear stress of the ER fluid made from Ni/(TiO₂+Urea) particles reaches 40kPa (the DC electric field is 4kV/mm), which is 10 times as high as that made from particles without urea. However, the shear stress decreases when excessive urea is added. The microstructure observation of the ER fluids under DC electric field shows that the particles aggregate to form thicker and dense column structure when the mass ratio of urea to Ti is 30%, while the column structure is broken when excessive urea (>30%) is added. A thin and loose column structure is formed in ER fluid without urea added. It is suggested that the ER behaviors is substantially correlated with the polar molecules in urea.

Key words: electrorheological effect, Ni nanoparticle, polar molecule, TiO₂

中图分类号:

TB381

杨建国,纪松,孟庆伟,谭锁奎,郭红燕,赵红. Ni/（TiO^₂+Urea）纳米核壳颗粒电流变行为[J]. 无机材料学报, DOI: 10.3724/SP.J.1077.2010.00259.

YANG Jian-Guo,JI Song,MENG Qing-Wei,TAN Suo-Kui,GUO Hong-Yan,ZHAO Hong. Electrorheological Behavior of Ni/（TiO^₂+Urea）Core-shell Nano Particles[J]. Journal of Inorganic Materials, DOI: 10.3724/SP.J.1077.2010.00259.

参考文献

［1］Block H, Kelly J P．Electrorheology．J．Phys. D：Appl．Phys., 1988, 21： 1661-1667.

［2］Halsay T C．Electrorheological fluids. Science, 1992, 258(5083)： 761-766．

［3］Whittle M, Bullough W A．The structure of smart fluids．Nature, 1992, 385：373．

［4］王宝祥, 左朝阳, 赵晓鹏（WANG Bao-Xiang, et al）．改性高岭土/氧化钛复合材料的制备及其高电流变活性. 无机材料学报（Journal of Inorganic Materials）, 2004, 19（4）： 886-870．

［5］Yin J B, Zhao X P．Preparation and enhanced electrorheological activity TiO₂ doped with chromium lon. Chem. Mater., 2004, 16（2）：321-328．

［6］路阳, 王学昭, 王风平, 等. 电流变液研究新进展. 材料导报, 2009, 23（2）： 6-8.

［7］庞雪蕾, 唐芳琼(PANG Xue-Lei, et al)．电流变液体的研究进展. 化学进展(Prog. Chem.), 2004, 16（6）： 849-857．

［8］乔荫颇, 尹剑波, 赵晓鹏. 表面改性纳米氧化钛的强电流变效应. 材料研究学报, 2006, 20（4）： 417-421.

［9］赵艳, 王宝祥, 赵晓鹏(ZHAO Yan, et al). Cr离子改性氧化钛/丙烯酰胺纳米电流变液及其性能研究. 无机材料学报（Journal of Inorganic Materials）, 2006, 21（3）： 671-675.

［10］王学昭, 沈容, 温维佳, 等. 钛酸钙体系电流变液的研究. 功能材料, 2006, 37（5）： 681-683.

［11］Conrad H, Wit C W, Tang X, Conductivity in electrorheology. in Proc．of the 6th Iht．Conf on ERF, MR suspensions and their Applications, Nakano M, Koyama K. ed. Singapore: World Scientific, 1998, 77.

［12］Wu C W, Conrad H．Multicoated spheres: recommended electrorheological particles．J．Phys. D：Appl., 1998, 31： 3312-3315．

［13］Tam W Y, Yi G H, Wen W J, et al．New electrorheological fluid: theory and experiment．Phys. Rev. Lett., 1997, 78（15）： 2987-2990．

［14］Men S, Xu X, Lan Y, et al．The electrostatic interaction between coated particle in a host liquid．In：Tao R, Shaw S eds．Proc．7th Inter．Conf． on ER Fluids and MR Suspensions．Hono2 lala Hawaii, 1999, 246-251．

［15］温维佳, 黄先祥, 杨世和, 等(WEN Wei-Jia, et al)．巨电流变效应及其机理. 物理（Physics）, 2003, 32（12）： 777-779．

［16］Wu C W, Conrad H．Shear strength of electrorheological particle clusters．J．Mater. Sci. Eng. A, 1998, 248： 161-164．

［17］刘秧生, 官建国, 马会茹．聚苯胺修饰草酸氧钛钡电流变性能的研究. 功能材料, 2008, 39（11）: 1832-1834．

［18］Lu K Q, Shen R, Wang X Z, et al．Polak molecule type electrorheological fluids. Int. J. Mod. Phys. B, 2007, 21（28/29）： 4798-4805．

［19］Shen R, Wang B Z, Wen W J. TiO₂ based electrorheological fluid with high yield stress, et al．Int. J． Mod. Phys. B, 2005, 19（7/ 8/9）： 1104-1109．

［20］Lu K Q, Shen R, Wang W J, et al．The electrorheological fluids with high shear stress. Int. J． Mod.Phys. B, 2005, 19（7/8/9）： 1065-1070．

[1]	薛虹云, 王聪宇, MAHMOOD Asad, 于佳君, 王焱, 谢晓峰, 孙静. 二维g-C₃N₄与Ag-TiO₂复合光催化剂降解气态乙醛抗失活研究[J]. 无机材料学报, 2022, 37(8): 865-872.
[2]	迟聪聪, 屈盼盼, 任超男, 许馨, 白飞飞, 张丹洁. SiO₂@Ag@SiO₂@TiO₂核壳结构的制备及其光催化降解性能[J]. 无机材料学报, 2022, 37(7): 750-756.
[3]	潘碧宸,任鹏禾,周特军,蔡圳阳,赵小军,周宏明,肖来荣. 树脂基复合材料表面隔热涂层的组织与性能研究[J]. 无机材料学报, 2020, 35(8): 947-952.
[4]	朱本必,张旺,张志坚,章建忠,IMRAN Zada,张荻. 光热增强光催化性能二氧化钛(B)/玻纤布复合研究[J]. 无机材料学报, 2019, 34(9): 961-966.
[5]	李远洋,江波. 具有超亲水光催化性能的λ/4-λ/2型两层宽频增透膜的制备和性能研究[J]. 无机材料学报, 2019, 34(2): 159-163.
[6]	苏琨, 张亚茹, 陆飞, 张君, 王熙. 铂修饰二氧化钛纳米片的制备及其光电催化析氢反应研究[J]. 无机材料学报, 2019, 34(11): 1200-1204.
[7]	盛鹏, 赵广耀, 徐丽, 刘双宇, 王博, 刘海镇, 马光, 韩钰, 陈新. 铝沉积还原制备蓝色二氧化钛[J]. 无机材料学报, 2018, 33(9): 942-948.
[8]	范闻, 武利民. 硅油两步脱水法可控制备纳米二氧化钛透镜[J]. 无机材料学报, 2018, 33(12): 1337-1342.
[9]	林景诚, 唐笑, 楚婉怡. 液相合成超小TiO₂纳米簇及其光催化性质[J]. 无机材料学报, 2017, 32(8): 863-869.
[10]	鲍艳, 康巧玲. 中空TiO₂微球的制备及其对聚丙烯酸酯薄膜保温性能的影响[J]. 无机材料学报, 2017, 32(6): 581-586.
[11]	李翠霞, 金海泽, 杨志忠, 杨轩, 董其铮, 厉婷婷. 介孔RGO/TiO₂复合光催化材料的制备及光催化性能[J]. 无机材料学报, 2017, 32(4): 357-364.
[12]	喻洋, 佟明兴, 何玉兰, 陈辉, 高静, 李国华. 介孔TiO₂/WO₃空心球的制备及其可见光光催化性能[J]. 无机材料学报, 2017, 32(4): 365-371.
[13]	马雅婷, 李巧玲. TiO₂/Co₃O₄复合纳米颗粒的制备及其光催化制氢性能[J]. 无机材料学报, 2016, 31(8): 841-844.
[14]	徐双双, 陈功, 张海琴, 陈元, 肇研. Ni-RGO纳米吸波材料的制备及其电磁行为研究[J]. 无机材料学报, 2016, 31(6): 567-574.
[15]	王慧蕾, 刘孝恒. 银粒子修饰下的介孔二氧化钛的制备及其光催化性能的研究[J]. 无机材料学报, 2016, 31(5): 555-560.

Ni/（TiO^₂+Urea）纳米核壳颗粒电流变行为

Electrorheological Behavior of Ni/（TiO^₂+Urea）Core-shell Nano Particles

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价