载体对铂基疏水催化剂活性的影响

doi:10.3724/SP.J.1077.2010.00279

摘要/Abstract

摘要： 为了研究载体对铂（Pt）基疏水催化剂活性的影响, 分别选取了炭黑、SiC纳米粉、铈锆复合氧化物(Ce _0.4 Zr _0.6 O₂-γ-Al₂O₃)等三种物质, 在氯铂酸的乙二醇溶液中, 用高压微波加热法制备了Pt基催化剂, 然后将其与聚四氟乙烯一起负载于泡沫镍上, 制成疏水催化剂. 用X射线衍射、透射电子显微镜、X光电子能谱、扫描电子显微镜等方法分析了催化剂的结构与组成, 并研究了疏水催化剂对氢氧复合反应及氢水交换反应的催化活性. 结果表明：Pt在载体表面分布均匀, 在Pt/C、Pt/SiC、Pt/Ce _0.4 Zr_0.6 O₂-γ-Al₂O₃中Pt的平均粒径分别为4.46、1.67和1.77nm; Pt/C、Pt/SiC催化剂中Pt存在Pt（0）、Pt（Ⅱ）和Pt（Ⅳ）三种价态; Pt/C、Pt/SiC在泡沫镍表面的分布均匀, 而Pt/Ce _0.4 Zr_0.6 O₂-γ-Al₂O₃分布不均匀. Pt/C/FN对氢氧复合反应和氢水交换反应的催化活性都较高; Pt/SiC/FN和Pt/Ce _0.4 Zr_0.6 O₂-γ-Al₂O₃/FN对氢氧复合反应的催化活性高, 但是对氢水交换反应的催化活性很低.

关键词: 铂基催化剂, 疏水催化剂, 炭黑, 纳米碳化硅, 铈锆复合氧化物γ氧化铝

Abstract: In order to study the influence of carriers on platinum(Pt) based hydrophobic catalysts’ activity, and explore the practicability of applying silicon carbide and ceriumzirconium composite oxides as carriers of hydrophobic catalysts, Pt based catalysts were prepared by microwave heating method, with carbon black, nanometer SiC and Ce _0.4 Zr_0.6 O₂-γ-Al₂O₃ as carriers, respectively. Then Pt based catalysts were loaded on foam nickel (FN) with polytetrafluoroethylene latex, and hydrophobic catalysts were obtained. Structure of catalysts was analyzed by XRD, TEM, XPS, SEM, etc, moreover, their catalytic activity for recombination of H₂-O₂ and hydrogen-water liquid catalytic exchange was tested. Results show that Pt particles are evenly distributed on carriers’ surface, and average size of Pt particles in Pt/C, Pt/SiC and Pt/Ce _0.4 Zr_0.6 O₂-γ-Al₂O₃are 4.46, 1.67 and 1.77nm, respectively. Three valences, Pt (0), Pt (Ⅱ) and Pt (Ⅳ) exist in Pt/C and Pt/SiC catalysts. Pt/C and Pt/SiC catalyst particles are evenly distributed on the surface of foam nickel, but it is not the case for Pt/Ce _0.4 Zr_0.6 O₂-γ-Al₂O₃. The catalytic activity of Pt/C/FN is quite high for both recombination of H₂-O₂ and hydrogenwater liquid catalytic exchange. The catalytic activities of Pt/SiC/FN and Pt/Ce _0.4 Zr_0.6 O₂-γ-Al₂O₃/FN are high for recombination of H₂-O₂, however, they are quite low for hydrogen-water liquid catalytic exchange.

Key words: platinum based catalyst, hydrophobic catalyst, carbon black, nanometer silicon carbide, cerium-zirconium composite oxide-γ-alumina

中图分类号:

O614

熊亮萍,胡胜,任兴碧,罗阳明. 载体对铂基疏水催化剂活性的影响[J]. 无机材料学报, DOI: 10.3724/SP.J.1077.2010.00279.

XIONG Liang-Ping,HU Sheng,REN Xing-Bi,LUO Yang-Ming. Influence of Carrier on Catalytic Activity of Platinum Based Hydrophobic Catalysts[J]. Journal of Inorganic Materials, DOI: 10.3724/SP.J.1077.2010.00279.

参考文献

［1］胡胜, 罗阳明, 王和义, 等. 疏水催化剂应用进展.原子能科学技术, 2006, 40(6): 671-676.

［2］Li J, Suppiah S, Kutchcoskie K. Wetproofed Catalysts for Hydrogen Isotope Exchange. US Patent: 2004/0248735 A1, 2004.12.09.

［3］Antolini E, Cardellini F, Giacometti E, et al. Study on the formation of Pt/C catalysts by non-oxidized active carbon support and a sulfurbased reducing agent. J. Mater. Sci., 2002, 37(1): 133-139.

［4］Stoyanova A, Naidenov V, Petrov K, et al. Effect of preparation conditions on the structure and catalytic activity of carbon-supported platinum for the electrooxidation of methanol. J. Appl. ElectroChem., 1999, 29(10): 1197-1203.

［5］Wine G, Ledoux M J, Cuong P H. Supported BETA zeolite on preshaped β-SiC as clean friedel-crafts liquid-phase catalyst. Top. in Catal., 2007, 45(1-4): 111-116.

［6］Pesant L, Matta J, Garin F, et al. A high-performance Pt/β-SiC catalyst for catalytic combustion of model carbon particles (CPs). Appl. Catal. AGen., 2004, 266(11): 21-27.

［7］Nhut J M, Pesant L, Keller N, et al. Pd/SiC exhaust gas catalyst for heavy-duty engines: improvement of catalytic performances by controlling the location of the active phase on the support. Top. in Catal., 2004, 30-31(1): 353-358.

［8］Gatica J M, Baker R T, Fornasiero P, et al. Rhodium dispersion in a Rh/Ce _0.68 Zr _0.32 O₂ catalyst investigated by HRTEM and H₂ chemisorption. J. Phys. Chem. B, 2000, 104(19): 4667-4672.

［9］肖莉, 林培琰, 杨志柏, 等. Ce-Zr固溶体的纯度及其在三效催化剂中的作用. 分子催化, 2000, 14(2): 81-86.

［10］万李, 吴晓东, 樊俊, 等(WAN Li, et al). 制备方法对钯铈锆固溶体催化剂的结构与性能的影响. 中国稀土学报(J. Rare Earth), 2004, 24(4): 522-526.

［11］Wang K, Li X J, Ji S F, et al. Effect of Ce _xZr _1-x O₂ promoter on Nibased SBA-15 catalyst for steam reforming of methane. Energy Fuels, 2009, 23(1): 25-31.

［12］杨修春, 卢振光, 康晓春, 等(YANG Xiu-Chun, et al). ZrO₂对NiO/CeO₂/γAl₂O₃复合催化剂结构的影响. 无机材料学报(Journal of Inorganic Materials), 2009, 24(1): 187-191.

［13］胡胜. 高分散度Pt基疏水催化剂制备及氢水液相催化交换性能研究. 绵阳: 中国工程物理研究院核物理与化学研究所博士论文, 2007.

[1]	谢仰恩, 王丁玲, 马兆昆, 宋怀河, XUPei. 微生物燃料电池Fe-N掺杂炭黑阴极催化剂性能研究[J]. 无机材料学报, 2018, 33(3): 295-300.
[2]	王三海, 江伟辉, 冯果, 刘健敏, 苗立锋, 王洪达. 以炭黑为还原剂制备硅酸锆晶须的研究[J]. 无机材料学报, 2014, 29(8): 835-838.
[3]	叶林森,罗德礼, 杨莞, 郭文胜, 徐钦英, 罗丽珠. 铂基疏水催化剂制备及其在氢-水液相催化交换中的应用[J]. 无机材料学报, 2014, 29(4): 387-392.
[4]	彭诚, 张楚鑫, 吕明, 李智鸿, 吴建青. 共沉淀法制备硅酸锆包裹炭黑及其高温稳定性[J]. 无机材料学报, 2013, 28(8): 847-852.
[5]	王莉, 罗发, 刘莉, 周万城, 朱冬梅. CB/PBO复合材料制备及吸波性能研究[J]. 无机材料学报, 2013, 28(12): 1333-1337.
[6]	刘保荣, 黄智斌, 罗发, 钱七虎. 碳/氧化铝/二氧化硅涂层的介电和吸波性能研究[J]. 无机材料学报, 2012, 27(8): 817-821.
[7]	曾洪, 阚艳梅, 徐常明, 王佩玲, 张国军. 固相反应法合成碳化硼纳米粉体[J]. 无机材料学报, 2011, 26(10): 1101-1104.
[8]	熊亮萍, 胡胜, 侯京伟, 翁葵萍, 罗阳明, 杨通在. 铁系元素掺杂的Pt基疏水催化剂的制备及活性研究[J]. 无机材料学报, 2011, 26(1): 91-96.
[9]	刘淼,黄剑锋,王博,曹丽云,吴建鹏. C/C复合材料表面水热电泳沉积SiC_n/SiC复合抗氧化涂层研究[J]. 无机材料学报, 2009, 24(6): 1214-1218.
[10]	李芳菲,蒋引珊,夏茂盛,孙萌萌,薛兵,刘大锐. 纳米白炭黑对介孔蒙脱石水热稳定性的增强作用[J]. 无机材料学报, 2009, 24(5): 1025-1030.
[11]	于威,杜洁,张丽,崔双魁,路万兵,傅广生. 氢流量对纳米SiC薄膜微结构和光学特性的影响[J]. 无机材料学报, 2008, 23(3): 540-544.
[12]	赵木,宋怀河,连文涛,陈晓红,田晓冬,陈磊. 金属对炭黑转化为洋葱状中空结构纳米碳的影响[J]. 无机材料学报, 2007, 22(4): 599-603.
[13]	陈晓东,王桂芹,段玉平,李伟平,刘顺华. 壳-芯型复合陶瓷材料的制备及其电磁特性[J]. 无机材料学报, 2007, 22(3): 456-460.
[14]	符冬菊,刘旭光,杜爱兵,韩培德,贾虎生,许并社. 微波等离子体法合成洋葱状富勒烯的研究[J]. 无机材料学报, 2006, 21(3): 576-582.
[15]	高濂,王宏志,洪金生,宫本大树,DIAZ DE LA TORRE Sebastian. 放电等离子超快速烧结SiC-Al₂O₃纳米复相陶瓷[J]. 无机材料学报, 1999, 14(1): 55-60.