氟化铅晶体的生长与Cherenkov辐射特性

无机材料学报

氟化铅晶体的生长与Cherenkov辐射特性

沈定中; 任国浩; 王绍华; 邓群; 殷之文

中国科学院上海硅酸盐研究所; 上海 200050

收稿日期:1998-01-02 修回日期:1998-03-23 出版日期:1999-02-20 网络出版日期:1999-02-20

Growth And Cherenkov Radiation Characteristics of PbF₂Crystals

SHEN Ding-Zhong; REN Guo-Hao; WANG Shao-Hua; DENG Qun; YIN Zhi-Wen

Shanghai Institute of Ceramics; Chinese Academy of Sciences Shanghai 200050 China）

Received:1998-01-02 Revised:1998-03-23 Published:1999-02-20 Online:1999-02-20

摘要/Abstract

摘要： 采用脱氧剂非真空坩埚下降法生长出的大尺寸PbF₂晶体具有优异的Cherenkov辐射特性，其透光截止波长最短可达245um，能量分辨率优于32％／E^1/2，辐照损伤很弱，用365um的过滤光漂白后，透光能力几乎可以完全恢复到辐照之前的水平．

关键词: PbF₂晶体, Cherenkov辐射, 截止波长, 能量分辨率, 辐照损伤

Abstract: A large size PbF₂ crystal was grown with the modified non-vacuum Bridgeman method. Itpossesses outstanding Cherenkov radiation properties. Its cut-off edge is as short as 245urn, theenergy resolution is superior to 3.2%/E^1/2, and the radiation damage is weak and can be cured byannealing with 365um filtered light.

Key words: PbF₂ crystal, Cherenkov radiation, cut-off edge, energy resolution, radiation damage

中图分类号:

沈定中,任国浩,王绍华,邓群,殷之文. 氟化铅晶体的生长与Cherenkov辐射特性[J]. 无机材料学报.

SHEN Ding-Zhong,REN Guo-Hao,WANG Shao-Hua,DENG Qun,YIN Zhi-Wen. Growth And Cherenkov Radiation Characteristics of PbF₂Crystals[J]. Journal of Inorganic Materials.

[1]	王华进, 寇华敏, 王墉哲, 姜大朋, 张博, 钱小波, 王静雅, 朱琳玲, 曾爱军, 杨秋红, 苏良碧. 193 nm激光下不同含量Y杂质CaF₂晶体辐照损伤研究[J]. 无机材料学报, 2023, 38(2): 219-224.
[2]	欧阳琴, 王艳菲, 徐剑, 李寅生, 裴学良, 莫高明, 李勉, 李朋, 周小兵, 葛芳芳, 张崇宏, 何流, 杨磊, 黄政仁, 柴之芳, 詹文龙, 黄庆. 核用碳化硅纤维增强碳化硅复合材料研究进展[J]. 无机材料学报, 2022, 37(8): 821-840.
[3]	薛军明,刘茜. 离子晶体透红外截止波长的拓扑研究[J]. 无机材料学报, 2006, 21(6): 1301-1306.
[4]	肖海斌,胡关钦,徐力. 生长温度梯度对Bi₄Ge₃O₁₂晶体辐照损伤的影响[J]. 无机材料学报, 2003, 18(2): 470-474.
[5]	李泽逵,任国浩,沈定中,陈晓峰,殷之文. PbF₂晶体失透问题的研究[J]. 无机材料学报, 2002, 17(3): 455-459.
[6]	任国浩,沈定中,王绍华,刘光煜,倪海洪,殷之文. PbF₂:Gd晶体的发光强度与发光均匀性研究[J]. 无机材料学报, 2001, 16(1): 49-55.