AIN-多型体对形成长颗粒α-Sialon的影响

无机材料学报

AIN-多型体对形成长颗粒α-Sialon的影响

陈卫武; 孙维莹; 严东生

中国科学院上海硅酸盐研究所高性能陶瓷和超微结构国家重点实验室, 上海 200050

收稿日期:1999-01-28 修回日期:1999-03-23 出版日期:2000-02-20 网络出版日期:2000-02-20

Effect of AIN-polytypoid on Elongated α-Sialon Formation

CHEN Wei-Wu; SUN Wei-Ying; YAN Dong-Sheng

State key Lab of High Performance Ceramics and Superfine Microstructure; Shanghai Institute ofCeramics; Chinese Academy of Sciences; Shanghai 200050; China

Received:1999-01-28 Revised:1999-03-23 Published:2000-02-20 Online:2000-02-20

摘要/Abstract

摘要： 通过ＳＥＭ、ＥＤＳ等方法，研究了添加不同含量ＡＩＮ－多型体对（Ｙ＋Ｓm）－α－Ｓｉａｌｏｎ晶粒形貌的影响．结果表明，随ＡＩＮ－多型体添加量增多，材料中长颗粒α－Ｓｉａｌｏｎ的数量增加．本文对ａ’－ＡＩＮ－多型体两相区内长颗粒α－Ｓｉａｌｏｎ的形成机理进行了讨论．

关键词: 长颗粒α－Sialon, 形成机理, AIN－多型体

Abstract: The microstructural characteristic of (Y+Sm) α-Sialon with different amount of AINpolytypoid was studied by SEM and EDS. The formation mechanism of elongated α-Sialon inα -AIN-polytypoids dual-phases area was discussed. The results show that with increasing amountof AIN-polytypoid, more α-Sialon grains exhibit the enlongated morphology.

Key words: elongated α-Sialon, formation mechanism, AIN-polytypoid

中图分类号:

TQ163

陈卫武,孙维莹,严东生. AIN-多型体对形成长颗粒α-Sialon的影响[J]. 无机材料学报.

CHEN Wei-Wu,SUN Wei-Ying,YAN Dong-Sheng. Effect of AIN-polytypoid on Elongated α-Sialon Formation[J]. Journal of Inorganic Materials.

[1]	张叶, 姚冬旭, 左开慧, 夏咏锋, 尹金伟, 曾宇平. 原位引入BN-SiC燃烧合成Si₃N₄-BN-SiC复合材料[J]. 无机材料学报, 2022, 37(5): 574-578.
[2]	李春艳, 刘雪华, 刁飞玉, 梁文双, 王乙潜, PETROV Peter, ALFORD Neil. 钛酸锶钡薄膜中微观结构缺陷及其形成机理[J]. 无机材料学报, 2012, 27(3): 285-290.
[3]	谈国强,刘剑,苗鸿雁,贺中亮,夏傲. 四方相BaTiO₃薄膜的自组装制备与表征[J]. 无机材料学报, 2009, 24(4): 749-754.
[4]	田从学,张昭. 工业硫酸氧钛合成有序介孔TiO₂及其机理研究[J]. 无机材料学报, 2009, 24(2): 225-228.
[5]	倪良,张莉,王学宝. W/O乳状液模板法制备纳米MnO₂微球[J]. 无机材料学报, 2007, 22(1): 167-169.
[6]	陈文,麦立强,徐庆,彭俊锋,朱泉峣,余华. 氧化钒纳米管的自组装合成机理[J]. 无机材料学报, 2005, 20(1): 65-70.
[7]	李雅文,王佩玲,严东生,程一兵. Si₃N₄原料对形成长颗粒Ca-α-Sialon晶粒形貌的影响[J]. 无机材料学报, 2000, 15(1): 62-66.