Journal of Inorganic Materials
• Research Paper • Previous Articles Next Articles
XIA Jin-Tong; CHEN Xiao-Hua; ZHENG Mao-Ping; XIONG You-Yi; ZHOU Sheng-Mai; CHEN Zong-Zhang
Received:
Revised:
Published:
Online:
Abstract: Fluorine gas was produced with the electrolysis of the molten salt KF·2HF, then graphite fluoride was prepared through the reaction between graphite powder and fluorine gas at 500℃. The real density of the graphite fluoride was 2.53g/cm^3, its electrical resistivity 3.1×103Ω·cm and its colour greyish white. The graphite fluoride synthesized had a absorption peak of infrared reflection spectra on F--C covalent bond at approximation wavenumber 1219cm-1 and 1350cm-1. By testing friction factor for the graphite fluoride, graphite powder and molybdenum disulphide, the experimental results showed that the friction factor of the graphite fluoride was the smollest. Furthermore, technological conditions and special properties of the graphite fluoride were dissussed.
Key words: preparation of fluorine gas, graphite fluoride, friction properties
CLC Number:
O613
TQ124
XIA Jin-Tong,CHEN Xiao-Hua,ZHENG Mao-Ping,XIONG You-Yi,ZHOU Sheng-Mai,CHEN Zong-Zhang. A New Type of the Solid Lubricant Material-Preparation and Properties of Graphite Fluoride[J]. Journal of Inorganic Materials.
0 / / Recommend
Add to citation manager EndNote|Ris|BibTeX
URL: https://www.jim.org.cn/EN/
https://www.jim.org.cn/EN/Y1998/V13/I3/435