Research Progress on TeO2 Crystal and Its Utilization in Infrared Devices

doi:10.15541/jim20140557

Abstract

Abstract:

TeO₂ crystal has excellent acousto-optic properties and double b decay properties of high natural abundance of ¹³⁰Te isotope. It can be used in high-performance acousto-optic devices and also for the research of neutrino and dark matter. Recently, the above applications raise the requirements for the size and quality of TeO₂ crystal. Structure and physical properties of TeO₂ crystal are briefly introduced in this article, and then the recent progress on the preparation of large sized TeO₂ crystal with high quality and its application in infrared devices are reviewed. Finally, its preparation and application in future of TeO₂ crystal are discussed.

Key words: TeO2 crystal, preparation, infrared devices, revie

CLC Number:

TQ174

ZHU Yong, YUE Shi-Hai, WANG Wei, YIN Xue-Ji, GE Zeng-Wei. Research Progress on TeO₂ Crystal and Its Utilization in Infrared Devices[J]. Journal of Inorganic Materials, 2015, 30(8): 802-808.

Figures/Tables 7

Fig. 1 Sketch map of the structure of a TeO2 crystal (a) along <110> and (b) <001> orientations [9]

Table 1 Acousto-optic (AO) properties of some typical AO materials[12]

Material	Direction of propagation	Sound velocity/ (×10⁵, cm·s^-1)	AO merit M₂/(×10^-18, s³·g^-1)
Fused silica	-	5.960	1.0
LiNbO₃ crystal	<100>	6.570	4.6
PbMoO₄crystal	<001>	3.362	36.1
PbBr₂crystal	<010>	0.650	550.0
Hg₂Cl₂crystal	<110>	0.347	700.0
TeO₂crystal	<110>	0.616	793.0

Fig. 2 PtTe2 crucible prepared by the reaction between Pt and TeO2 powder at 1147℃[21]

Fig. 3 Melt character istics when (a) R=1.8 cm, ω=1.36 s-1 and (b) R=3.2 cm, ω=1.36 s-1 [29]

Fig. 4 TeO2 crystal grown by Bridgman method[9]

Fig. 5 Flow chart of the manufacturing method for the high- purity TeO2 single crystal[35]

Fig. 6 Schematic of noncollinear AOTF[43]

References 57

[1]	LIEBERTZ J.Einkristallzüchtung von paratellurit (TeO2).Kristall und Technik, 1969, 4(2): 221-225.
[2]	MIYAZAWA S, IWASAKI H.Single crystal growth of paratellurite TeO2.Jpn. J. Appl. Phys., 1970, 9(5): 441-445.
[3]	UCHIDA N.Optical properties of single-crystal paratellurite (TeO2).Phys. Rev. B, 1971, 4(10): 3736-3745.
[4]	PEERCY P S, FRITZ I J.Pressure-induced phase transition in paratellurite (TeO2).Phys. Rev. Lett., 1974, 32(9): 466-469.
[5]	FRITZ I J, PEERCY P S.Phenomenological theory of the high-pressure structural phase transition in paratellurite (TeO2).Solid State Commun., 1975, 16(10/11): 1197-1200.
[6]	SKELTON E F, FELDMAN J L, LIU C Y, et al.Study of the pressure-induced phase transition in paratellurite (TeO2).Phys. Rev. B, 1976, 13(6): 2605-2613.
[7]	CAI QI-SHAN.Structure and physical properties of TeO2 crystal.Piezoelectrics & Acoustooptics, 1981, 2: 55-59.
[8]	DAFENEI I, DIEMOZ M, LONGO E, et al.Growth of pure and doped TeO2 crystals for scintillating bolometers.Nucl. Instrum. Meth. A, 2005, 554(1/2/3): 195-200.
[9]	Chu Y Q, Li Y G, Ge Z W, et al.Growth of the high quality and large size paratellurite single crystals. J. Cryst. Growth, 2006, 295(2): 158-161.
[10]	CHU YAO-QING, GE ZENG-WEI, WU GUO-QING, et al.Growth of acousto-optic TeO2 single crystal with large size and high quality.Journal of Synthetic Crystals, 2004, 33(5): 810-812.
[11]	JI XIAO-HONG, SANG WEN-BIN, LIU DONG-HUA, et al.Study on Czochralski growth of TeO2 single crystal and defects.Journal of Synthetic Crystals, 2001, 30(1): 93-98.
[12]	REN QUAN, HUAN HUI.Growth and characterization of two new types of acousto-optic crystals.Piezoelectrics & Acoustooptics, 1993, 15(5): 33-37.
[13]	GIULIANI A.Searches for neutrinoless double beta decay.Acta Phys. Polonica B, 2010, 41(7): 1447-1468.
[14]	ANDREOTTI E, ARNABOLDI C, AVIGNONE III F T, et al. 130Te neutrinoless double-beta decay with CUORICINO.Astropart. Phys., 2011, 34(11): 822-831.
[15]	PREVITALI E. Search for neutrinoless double beta decay with CUORE. Nucl. Instrum. Meth. A, 2013, 718: 522-523.
[16]	ARNABOLDI C, BROFFERIO C, BRYANT A, et al.Production of high purity TeO2 single crystals for the study of neutrinoless double beta decay.J. Cryst. Growth, 2010, 312(20): 2999-3008.
[17]	CANONICA L, ARTUSA D R, AVIGNONE III F T, et al. First CUORE-0 performance results and status of CUORE experiment.J. Low. Temp. Phys., 2014, 176(5/6): 986-994.
[18]	CASALI N, BELLINI F, DAFINEI I, et al.Monte Carlo simulation of the Cherenkov radiation emitted by TeO2 crystal when crossed by cosmic muons.Nucl. Instrum. Meth. A, 2013, 732: 338-341.
[19]	BELLINI F, CASALI N, DAFINEI I, et al.Measurements of the Čerenkov light emitted by a TeO2 crystal.J. Inst., 2012, 7: P11014.
[20]	BEAUDRY J N, GRENIER S, AMRATE S, et al.Synthesis of high purity, stoichiometric controlled, TeO2 powders.Mater. Chem. Phys., 2012, 133(2/3): 804-807.
[21]	MANGIN J, VEBER P.PtTe2: Potential new material for the growth of defect-free TeO2 single crystals. J. Cryst. Growth, 2008, 310(12): 3077-3083.
[22]	ŁUKASIEWICZ T, MAJCHROWSKI A.Czochralski growth of TeO2 single crystals under conditions of forced convention in the melt.J. Cyst. Growth, 1992, 116: 364-368.
[23]	TOHOKU METAL IND LTD(TOHM-C). Tellurium Dioxide Single Crystal Growth - with the (100) Axis Set in the Draw Up Direction. Japan, C30B29/46, 61-174199A2, 1986.8.5.
[24]	ZHOU ZHE-YI, ZHANG HENG, XU SHOU-QI.Growth of large TeO2 single crystals by using czochralshi technique under pressure.Journal of Inorganic Materials, 1987, 2(3): 193-198.
[25]	QIAN XU-FA.Research on streak formation in growing single crystal with large size by CZ method.Journal of Synthetic Crystals, 1997, 26(3/4): 381.
[26]	KUMARAGURUBARAN S, KRISHNAMURTHY D, SUBRAM ANIAN C, et al.Growth of paratellurite crystals: effect of axial temperature gradient on the quality of the crystals.J. Cryst. Growth, 2000, 211(1-4): 276-280.
[27]	TAO SHAO-JUN, SANG WEN-BIN, QIAN YONG-BIAO, et al.Study on the influence of growth parameters on TeO2 single crystal quality.Journal of Synthetic Crystals, 2003, 32(2): 165-169.
[28]	KOLESNIKOV A I, SMIRNOV Y M, KAPLUNOV I A, et al. Czochralski’s method of growing paratellurite monocrystals from liquid melt. Russia, C30B29/16, RU2338816. 2008.11.20.
[29]	KOLESNIKOV A I, GRECHISHKIN R M, TRET’YAKOV S A, et al. Taylor vortices formed in the melt during paratellurite crystal growth.Crystallography Reports, 2008, 53(7): 1203-1207.
[30]	KOKH A E, SHEVCHENKO V S, VLEZKO V A, et al.Growth of TeO2 single crystals by the low temperature gradient Czochraski method with nonuniform heating.J. Cryst. Growth, 2013, 384: 1-4.
[31]	VERBER P, MANGIN J, STIMER P, et al.Bridgman growth of paratellurite single crystals.J. Cryst. Growth, 2004, 270(1/2): 77-84.
[32]	蒲芝芬, 葛增伟.二氧化碲单晶体的生长技术. 中国, C30B29/46, ZL85107803. 1989.09.13.
[33]	葛增伟, 吴国庆, 储耀卿, 等.一种二氧化碲单晶体的坩埚下降生长方法. 中国, C30B29/16, ZL03141999.2. 2007.03.21.
[34]	葛增伟, 朱勇, 吴国庆, 等.一种高纯二氧化碲单晶及制备方法. 中国, C30B15/00, ZL10048849. 2010.10.06.
[35]	GE Z W, ZHU Y, WU G Q,et al. High-purity Tellurium Dioxide Single Crystal and Manufacturing Method Thereof. US, C30B15/00, US008480996. 2012.03.22.
[36]	CHU YAO-QING, CHEN ZHI-ZHAN, LI YAO-GANG, et al.Defects of TeO2 crystals grown by Bridgman method.Journal of Synthetic Crystals, 2009, 38(2): 481-485.
[37]	CARDANI L, GIRONI L, BEEMAN J W, et al.Performance of a large TeO2 crystal as a cryogenic bolometer in searching for neutrinoless double beta decay.J. Inst., 2012, 7: P01020.
[38]	FANG YA-KE, SANG WEN-BIN, MIN JIA-HUA.Etching morphology and symmetry of TeO2 crystal.Journal of Inorganic Materials, 2004, 19(6): 1419-1422.
[39]	VOLOSHINOV V B, NIKITIN P A, TRUSHIN A S, et al.Acousto-optic cell based on paratellurite crystal with surface excitation of acoustic waves.Techn. Phys. Lett., 2011, 37(8): 754-756.
[40]	VEBER P, MANGIN J.TeO2 liquid phase: viscosity measurements and evaluation of the thermal conductivity from crystal growth experiments.Mater. Res. Bulletin, 2008, 43(11): 3066-3073.
[41]	CHEN SU-CHAO, LIU BO, WU XIAO-MIN. A review of studies on AOTF properties based on different dielectric materials. Study on Optical Communications.2011, 5: 56-59.
[42]	SUN ZHEN-DONG, DUAN QIAO-FENG, ZHAO YU-CHUN, et al.Design of infrared spectrometer with AOTF technique.Optical Technique, 2004, 30(5): 594-599.
[43]	LIN WEI, XUE FENG, ZHANG YE-HUI, et al.Acousto-optic tunable filter and its application.Microcomputer Information, 2005, 21(10): 127-128.
[44]	TRAN C D.Principles, instrumentation, and applications of infrared multispectral imaging, an overview.Analytical Letters, 2005, 38: 735-752.
[45]	HAO HUI-MIN, CAO JIAN-AN, YU ZHI-QIANG, et al.Exploratory research on quantitative analysis of gaseous mixtures by AOTF-NIR spectrometer.Spectroscopy and Spectral Analysis, 2009, 29(8): 2087-2091.
[46]	KORABLEV O, BERTAUX J L, GRIGORIEV A, et al.An AOTF-based spectrometer for the studies of Mars atmosphere for Mars express ESA mission.Adv. Space Res., 2002, 29(2): 143-150.
[47]	KORABLEV O, FEDOROVA A, BERTAUX J L, et al.SPICAV IR acousto-optic spectrometer experiment on venus express.Planetary Space Sci., 2012, 65(1): 38-57.
[48]	LEROI V, BIBRING J P, BERTHE M.Micromega/IR : design and status of a near-infrared spectral microscope for in situ analysis of Mars samples.Planetary Space Sci., 2009, 57(8-9): 1068-1075.
[49]	WANG JIAN-YU, HE ZHI-PING, XU RUI.Application of Imaging Spectrum Technology Base on AOTF in Deep-space Exploration. Proceedings of 2013 Shanghai International Symposium on Remote Sensing & Social Development, Shanghai, 2013: 13-23.
[50]	YU GUI-YING, YAO SHUAI, GUO TIAN-TAI, et al.Optimized design of AOTF mid-IR spectrometer based on Tracepro.Infrared and Laser Engineering, 2008, 37: 441-443.
[51]	LIU WEI, HE XIAO-LIANG, WANG ZHI-LIN, et al.Mid-infrared acousto-optic tunable filter.Piezoelectrics & Acoustooptics, 2011, 33(2): 178-181.
[52]	ZHU QIAN, WANG YUE-MING, WANG JIAN-YU, et al.Characteristics of background radiation of shortwave infrared imaging spectrometer based on AOTF.Infrared and Laser Engineering, 2012, 41(3): 575-579.
[53]	TAN JIAN-YAO, REN YU, TAN YONG, et al.Impact of the rotatory property of TeO2 crystal on its spectral characteristics.Infrared and Laser Engineering, 2013, 42(1): 195-199.
[54]	XING HUI, ZHAO HUI-JIE, CHENG XUAN, et al.Radiometric calibration of hyperspectral imaging spectrometer based on AOTF.Infrared and Laser Engineering, 2009, 38(2): 205-209.
[55]	HE ZI-JIAN, SHI JIA-MING, ZHAO DA-PENG, et al.Recognition of camouflaged target by hyperspectral imaging system based on acousto-optic tunable filter.Laser & Infrared, 2014, 44(7): 796-800.
[56]	GUPTA N, DAHMANI R.AOTF Raman spectrometer for remote detection of explosives.Spectrachimica Acta Patr A, 2000, 56(8): 1453-1456.
[57]	UCKERT K, CHANOVER N J, GLENAR D A, et al.A miniature AOTF-LDTOF spectrometer suite for the detection of biomarkers on planetary surfaces.Life Detection in Extraterrestrial Samples, 2012, 6042: 1-2.

Research Progress on TeO₂ Crystal and Its Utilization in Infrared Devices

RichHTML

PDF (PC)

Knowledge

Cited

Abstract

Cite this article

share this article

Figures/Tables 7

References 57

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	WEI Xiangxia, ZHANG Xiaofei, XU Kailong, CHEN Zhangwei. Current Status and Prospects of Additive Manufacturing of Flexible Piezoelectric Materials [J]. Journal of Inorganic Materials, 2024, 39(9): 965-978.
[2]	YANG Xin, HAN Chunqiu, CAO Yuehan, HE Zhen, ZHOU Ying. Recent Advances in Electrocatalytic Nitrate Reduction to Ammonia Using Metal Oxides [J]. Journal of Inorganic Materials, 2024, 39(9): 979-991.
[3]	LIU Pengdong, WANG Zhen, LIU Yongfeng, WEN Guangwu. Research Progress on the Application of Silicon Slurry in Lithium-ion Batteries [J]. Journal of Inorganic Materials, 2024, 39(9): 992-1004.
[4]	HUANG Jie, WANG Liuying, WANG Bin, LIU Gu, WANG Weichao, GE Chaoqun. Research Progress on Modulation of Electromagnetic Performance through Micro-nanostructure Design [J]. Journal of Inorganic Materials, 2024, 39(8): 853-870.
[5]	CHEN Qian, SU Haijun, JIANG Hao, SHEN Zhonglin, YU Minghui, ZHANG Zhuo. Progress of Ultra-high Temperature Oxide Ceramics: Laser Additive Manufacturing and Microstructure Evolution [J]. Journal of Inorganic Materials, 2024, 39(7): 741-753.
[6]	WANG Weiming, WANG Weide, SU Yi, MA Qingsong, YAO Dongxu, ZENG Yuping. Research Progress of High Thermal Conductivity Silicon Nitride Ceramics Prepared by Non-oxide Sintering Additives [J]. Journal of Inorganic Materials, 2024, 39(6): 634-646.
[7]	CAI Feiyan, NI Dewei, DONG Shaoming. Research Progress of High-entropy Carbide Ultra-high Temperature Ceramics [J]. Journal of Inorganic Materials, 2024, 39(6): 591-608.
[8]	WU Xiaochen, ZHENG Ruixiao, LI Lu, MA Haolin, ZHAO Peihang, MA Chaoli. Research Progress on In-situ Monitoring of Damage Behavior of SiC_f/SiC Ceramic Matrix Composites at High Temperature Environments [J]. Journal of Inorganic Materials, 2024, 39(6): 609-622.
[9]	ZHAO Rida, TANG Sufang. Research Progress of Ceramic Matrix Composites Prepared by Improved Reactive Melt Infiltration through Ceramization of Porous Carbon Matrix [J]. Journal of Inorganic Materials, 2024, 39(6): 623-633.
[10]	FANG Guangwu, XIE Haoyuan, ZHANG Huajun, GAO Xiguang, SONG Yingdong. Progress of Damage Coupling Mechanism and Integrated Design Method for CMC-EBC [J]. Journal of Inorganic Materials, 2024, 39(6): 647-661.
[11]	ZHANG Xinghong, WANG Yiming, CHENG Yuan, DONG Shun, HU Ping. Research Progress on Ultra-high Temperature Ceramic Composites [J]. Journal of Inorganic Materials, 2024, 39(6): 571-590.
[12]	ZHANG Hui, XU Zhipeng, ZHU Congtan, GUO Xueyi, YANG Ying. Progress on Large-area Organic-inorganic Hybrid Perovskite Films and Its Photovoltaic Application [J]. Journal of Inorganic Materials, 2024, 39(5): 457-466.
[13]	LI Zongxiao, HU Lingxiang, WANG Jingrui, ZHUGE Fei. Oxide Neuron Devices and Their Applications in Artificial Neural Networks [J]. Journal of Inorganic Materials, 2024, 39(4): 345-358.
[14]	BAO Ke, LI Xijun. Chemical Vapor Deposition of Vanadium Dioxide for Thermochromic Smart Window Applications [J]. Journal of Inorganic Materials, 2024, 39(3): 233-258.
[15]	HU Mengfei, HUANG Liping, LI He, ZHANG Guojun, WU Houzheng. Research Progress on Hard Carbon Anode for Li/Na-ion Batteries [J]. Journal of Inorganic Materials, 2024, 39(1): 32-44.